Abstract:Good gas permeability is an essential factor for the smooth operation and high performance in the lower part of the blast furnace. Under the present low carbon blast furnace smelting conditions, the coke layer is thinner, and the proportion of the molten metal in the coke layer is significantly higher, resulting in a major reduction in gas permeability, which seriously affects blast furnace operations. Also, the lower thickness of the coke layer weakens the process of solid-liquid carbon dissolution when the molten iron passes through the coke layer, which reduces the carbon content of the molten iron and further deepens the erosion of the refractory by the unsaturated molten iron. The carbon dissolution in the molten iron in a blast furnace core was measured by a high-temperature vacuum wettability test tool that analyzed the interface wetting activity between Fe−C melts with specific carbon mass fraction (3.8%, 4.3%, 4.8%) and 99.9% of high temperatures graphite plates. Besides, the scanning electron microscope (SEM) and energy dispersive spectroscopy (EDS) were used to analyze the graphite substrate’s carburizing morphology and carburizing distances. The results show that, with the increase of carbon content, the interface contact angle becomes bigger. The contact angle decreases with time, and eventually reaches a steady-state during the melting process, and the Fe−C melt with saturated carbon cannot be wet. The scanning electron microscopy analysis shows that a spherical cap-like depression is created by a cross-section of the Fe−C melt and the graphite substrate, and the radius and volume of the depression decrease with increasing carbon content. The study of the EDS scanning analysis shows that the amount of dissolved carbon atoms in the graphite substrate penetrates the Fe−C melt and decreases with increasing initial carbon concentration. The smaller the carburizing effect, the better the wetting is conducive to carbon mass transfer. It is found that by measuring carburizing of the carbon atoms in the graphite substrate into the Fe−C melt by calculating the surface energy reduces the surface energy between the two. Thus, the surface tension decreases and the melt spreads slowly with contact angle gradually decreasing during melting.

Impact of Zinc on Gasification Reaction and Post-Reaction Strength of Ferro-coke

Impact of Potassium on Gasification Reaction and Post-Reaction Strength of Ferro-coke

Performance influence study on blast furnace raw materials by zinc and pb

Influence of alkali metal K on the gasification reaction of ferro-coke with CO2

Interface Wetting Behavior Between Iron and Coke During the Carbon Dissolution Process in a Blast Furnace

Effects of Zinc on χ-Fe5C2 for Carbon Dioxide Hydrogenation to Olefins: Insights from Experimental and Density Function Theory Calculations

Synergetic Utilization of Zinc-Bearing Dust by Carbothermic Reduction-Roasting Process: Phase Transformation and Morphological Evolution

Evolution of Coke Microstructure and Metallurgical Properties During Graphitization in a Blast Furnace

Gasification of iron coke and cogasification behavior of iron coke and coke under simulated hydrogen-rich blast furnace condition

Numerical Investigation of the Limit of Coke Rate Reduction in an Ironmaking Blast Furnace (BF)

Experimental Study on Influence of Al2O3, CaO and SiO2 on Preparation of Zinc Ferrite

Volatilization Kinetics of Zinc from the Flotation Products of Low-Grade Lead–Zinc Oxide Ore during Carbothermic Reduction

Research on the Post-reaction Strength of Iron Coke Hot Briquette under Different Conditions

Investigation on Gasification Reaction Behavior and Kinetic Analysis of Iron Coke Hot Briquette under Isothermal Conditions

Effect of gasification reaction on pore structure, microstructure, and macroscopic properties of blast furnace coke

Application of High‐ and Low‐Reactivity Cokes in Hydrogen‐Rich Blast Furnaces

Thermodynamic and experimental study of high-temperature roasting of blast furnace gas ash for recovery of metallic zinc and iron

Synthetic zinc ferrite reduction by means of mixtures containing hydrogen and carbon monoxide

Uncovering the Electronic Effects of Zinc on the Structure of Fe5C2-ZnO Catalysts for CO2 Hydrogenation to Linear Α-Olefins

Influence of Iron Ore Addition on Metallurgical Reaction Behavior of Iron Coke Hot Briquette

The Effect of Zinc Addition on the Oxidation State of Cobalt in Co/ZrO2 Catalysts.