Abstract:Zinc extraction from oxide ore has been paid more and more attention to due to the exhaustion of zinc sulfide ore resources. In this work, the volatilization kinetics of Zn from the flotation products of low-grade lead–zinc oxide ore during carbothermal reduction in the temperature range of 900–1300 °C were investigated. The phase transformation in briquettes during the reduction process was investigated by XRD and EPMA. The results showed that the transformation of ZnS by CaO may begin within the temperature range of 900–1050 °C, with the main occurrence observed in the range of 1050–1250 °C. The kinetics behavior of Zn volatilization was associated with the phase transformation. The volatilization of Zn was controlled by the interfacial chemical reaction within 900–1150 °C. As the reaction proceeded, the generation of the product layers (CaS, FeS and new slag phase) impeded the internal diffusion of Zn, CO and CO2. At this time, internal diffusion served as the rate-controlling step for Zn volatilization in the range of 1150–1300 °C. Hence, a staged kinetics model of Zn volatilization during carbothermal reduction in the form of carbon-bearing briquettes was established, and the apparent rate constants (k(T)) and activation energies (Ea) were obtained. This work provides a scientific basis for the flotation products treatment by carbothermal reduction and is of great significance in improving the sustainability of resources in the zinc smelting industry.

What problem does this paper attempt to address?

This paper attempts to solve the problem of zinc volatilization kinetics during the carbothermal reduction process from the flotation products of low - grade lead - zinc oxide ores. Specifically, the paper focuses on the following aspects: 1. **Zinc extraction problem**: With the depletion of zinc sulfide ore resources, the extraction of zinc from zinc oxide ores has received increasing attention. This study focuses on the treatment of flotation products of low - grade lead - zinc oxide ores in Lanping, Yunnan, and explores the volatilization behavior of zinc during the carbothermal reduction process in the temperature range of 900 - 1300°C. 2. **Phase - change mechanism**: The phase - change situation inside the briquette during the carbothermal reduction process was studied. Through X - ray diffraction (XRD) and electron probe micro - analysis (EPMA), it was found that ZnS may start to transform in the range of 900 - 1050°C under the action of CaO, mainly occurring in the range of 1050 - 1250°C. The volatilization of zinc is closely related to these phase - changes. 3. **Kinetic behavior**: The kinetic behavior of zinc volatilization was studied. It was found that in the range of 900 - 1150°C, the volatilization of zinc is controlled by the interfacial chemical reaction; as the reaction progresses, the generated product layers (such as CaS, FeS and new slag phases) hinder the internal diffusion of Zn, CO and CO₂, and in the range of 1150 - 1300°C, internal diffusion becomes the rate - controlling step for zinc volatilization. 4. **Establishment of kinetic model**: Based on the above research, a multi - stage kinetic model of zinc during the carbothermal reduction process was established, and the apparent rate constant \(k(T)\) and activation energy \(E_a\) were obtained. 5. **Improvement of resource sustainability**: This study provides a scientific basis for the treatment of flotation products through carbothermal reduction, which is of great significance for improving the resource sustainability of the zinc smelting industry. In summary, this paper aims to provide theoretical support and technical guidance for the efficient treatment of flotation products of low - grade lead - zinc oxide ores by in - depth study of the volatilization kinetics of zinc during the carbothermal reduction process, thereby promoting the sustainable use of resources.

Volatilization Kinetics of Zinc from the Flotation Products of Low-Grade Lead–Zinc Oxide Ore during Carbothermic Reduction

Phase Transformation Analysis and Process Optimisation of Low-Grade Lead–Zinc Oxysulphide Ore Carbothermal Reduction

Synergetic Utilization of Zinc-Bearing Dust by Carbothermic Reduction-Roasting Process: Phase Transformation and Morphological Evolution

Thermodynamic Analysis and Experimental Reseach on Treatment of Low-grade Pb/Zn Oxide Ore by Vacuum Carbothermic Reduction

Reduction Roasting of High Iron-Bearing Zinc Calcine under a CO-CO2 Gas: an Investigation of the Chemical and Mineralogical Transformations

Recovery of zinc from zinc oxide dust containing multiple metal elements by carbothermal reduction

Thermodynamic analysis on iron-making process of zinc leaching residue by carbon reduction

Vacuum Carbothermal Reduction Kinetics of Zinc Oxide Ore

Synchronous Volatilization of Sn, Zn, and As, and Preparation of Direct Reduction Iron (DRI) from a Complex Iron Concentrate Via CO Reduction

Reduction kinetics of SnO2 and ZnO in the tin, zinc-bearing iron ore pellet under a 20%CO-80%CO2 atmosphere

Mechanisms and kinetics of zinc and iron separation enhanced by calcified carbothermal reduction for electric arc furnace dust

Zinc recovery from zinc calcine by selective reduction roasting and acid leaching

Study on the Reaction Mechanism of Multi-Source Metallurgical Dust for Zinc Extraction and Iron Enrichment

Difference of Zinc Volatility in Diverse Carrier Minerals: the Critical Limit of Blast Furnace Dust Recycle

The Phase Transformation Behavior of Goethite Residues under a Background of Co-processing Zinc Hydrometallurgical Waste in the Kivcet Process

Mineral Evolution Mechanism of Zinc-slag during High-temperature Reactive Process

Study on tin and zinc recovery and pellet preparation for blast furnace from iron concentrate containing tin and zinc

Phase Transformation Behavior of Lead and Zinc in the High-Lead Slag Reduction Process

A Novel Process for the Recovery of Zn and Pb From Electric Arc Furnace Dust Through Vacuum Carbothermal Reduction

Kinetic Analysis of Recovering Zinc from Electric Arc Furnace Dust by Vacuum Carbothermic Reduction at 20 Pa

Melting-reduction of Low-grade Zinc Oxide Ores