Abstract:The recovery of metal from copper slag is of great significance to the resource utilization of copper slag and the sustainable development of copper smelting industry. Currently, hydrometallurgy is the traditional method used to recover mineral metals. However, as copper slag is a silicate mineral, the traditional acid-leaching process of metal results in the leaching of Si, resulting in the formation of silica gel. The silica gel can inhibit the recovery of metal while making metal difficult to separate from Si and causing filtration problems. This study proposed a two-stage method (evaporation + water washing) to selectively recover Fe and Zn from copper slag. Under the optimal conditions (evaporation: H 2 SO 4 = 3 M; time = 60 min; temperature = 120°C; and liquid–solid ratio = 4; water washing: liquid–solid ratio = 5), the leaching efficiency of Fe, Zn, and Si reached 99.94 %, 97.40 %, and 0.15 % respectively. The separation mechanism was determined through mineral characterization (XRD, SEM, HRTEM-EDS, SAED, AFM, etc.) and the application of DLVO theory. It was found that H + destroyed the Fe 2 SiO 4 structure in copper slag during the evaporation stage, which promoted the release of Fe and Zn, forming soluble sulfate crystals. Simultaneously, evaporation increased the ion concentration, reducing the repulsive force between colloids, resulting in the aggregation and precipitation of silica gel into stable amorphous silica. After washing, soluble sulfate is dissolved in water. The recovered Fe can be processed to get red iron oxide (96.32 % purity), the Zn-containing solution can be recycled for electrolytic Zn, and the residue can be used to prepare geopolymer (52.47 MPa, 28 days). The two-stage method for recovering metals from copper slag is highly efficient and provides valuable insights into resource utilization of metals and Si in silicon-containing solid wastes.

Recovery of Zinc and Copper from Lead Slag by the Combined Process of Beneficiation and Roasting

Lead Recovery from Zinc Leaching Residue by Flotation

Recovery of Copper, Lead and Zinc from Copper Flash Converting Slag by the Sulfurization-Reduction Process

Recovery of valuable metals from electroplating sludge with reducing additives via vitrification

Thermodynamic analysis and process optimization of zinc and lead recovery from copper smelting slag with chlorination roasting

A Thermodynamic and Experimental Assessment of the Recovery of Copper, Iron, Zinc, and Lead from Copper Slag

Recovery of Zinc and Lead from Copper Smelting Slags by Chlorination Roasting

Recovery of lead and silver from zinc acid-leaching residue via a sulfation roasting and oxygen-rich chlorination leaching method

Efficient recovery of zinc and copper from copper smelting slag (CSS) by cooperative modification with a composite medium of FeS-O2

Recovery of valuable metals from copper slag

A Novel Technology for Separating Copper, Lead and Zinc in Flotation Concentrate by Oxidizing Roasting and Leaching

Enhanced recovery of zinc and lead by slag composition optimization in rotary kiln

Stepwise Utilization Process to Recover Valuable Components from Copper Slag

Extraction of Lead and Zinc from a Rotary Kiln Oxidizing Roasting Cinder

Recovery of copper from refining slags of copper fire anode furnace by waste acid leaching and CaO roasting process

Pyrometallurgical Recovery of Valuable Metals from Flue Dusts of Copper Smelter Through Lead Alloy

Separation and Extraction of Valuable Metals from Electroplating Sludge by Carbothermal Reduction and Low-Carbon Reduction Refining

Comprehensive Recovery of Valuable Metals from Lead-zinc Tailings by Flotation

Innovative technology and mechanism for comprehensive recovery of copper, nickel, zinc and iron in electroplating sludge

An efficient approach to utilize copper smelting slag: Separating nonferrous metals and reducing iron oxide at high temperature

Two-stage method recovery of metals from copper slag: Realize the resource utilization of all components