Abstract:Over 50 million tons of copper slag are produced worldwide annually. Stacking is currently the primary method used to treat copper slag, resulting in resource wastage and environmental issues. Using slag as a raw material in the steel industry is areasonablesolution. However, the presence of nonferrous metals degrades steel performance and corrodes smelting equipment, and the remaining slag poses environmental and sustainable challenges. Thus, this study focused on removal of nonferrous metals from copper slag and subsequent reduction of iron oxide. The experimental results showed that increasing the percentage of the chlorinating agent (calcium chloride), temperature, and duration, the removal percentage of copper initially increased linearly, then plateaued. The acidity coefficient had a marginal effect on copper removal percentage. The optimum chlorination roasting conditions were 13 % calcium chloride, 1373 K, and 0.5 h, resulting in removal percentages of 90.3 %, 81.9 %, and 82.7 % for copper, zinc, and lead, respectively. The appropriate oxygen partial pressure for chlorination roasting was 10-5-0.7 atm. The reduction percentage of iron oxide was approximately 82 % under roasting conditions of 1.5 h at 1373 K. Based on these results, a novel scheme for copper slag utilization is proposed that involves chlorination roasting for nonferrous metal removal, reduction roasting for iron oxide reduction, and melting to obtain molten iron and separate molten slag. The iron and slag are used for steel manufacturing and rock wool preparation, respectively. This scheme provides apromisingway to efficiently use copper slag, which will reduce primary resource consumption and pollution.

Recovery of Zinc and Lead from Copper Smelting Slags by Chlorination Roasting

Thermodynamic analysis and process optimization of zinc and lead recovery from copper smelting slag with chlorination roasting

Recovery of Zinc and Copper from Lead Slag by the Combined Process of Beneficiation and Roasting

Recovery of valuable metals from electroplating sludge with reducing additives via vitrification

Volatilization of Zn and Pb and Preparation of Integrated Micro-Electrolysis Filter from Copper Slag and Its Application for Removing Cr(VI) from Aqueous Solution.

Recovery of lead and silver from zinc acid-leaching residue via a sulfation roasting and oxygen-rich chlorination leaching method

Recovery of Copper, Lead and Zinc from Copper Flash Converting Slag by the Sulfurization-Reduction Process

Recovery of copper from refining slags of copper fire anode furnace by waste acid leaching and CaO roasting process

A Thermodynamic and Experimental Assessment of the Recovery of Copper, Iron, Zinc, and Lead from Copper Slag

Recovery of valuable metals from copper slag

A new eco-friendly approach for recovery of iron from copper smelting slag: Using CO2 and Cl2 recycling strategies

An efficient approach to utilize copper smelting slag: Separating nonferrous metals and reducing iron oxide at high temperature

Effective separation and recovery of Zn, Cu, and Cr from electroplating sludge based on differential phase transformation induced by chlorinating roasting

Enhanced recovery of zinc and lead by slag composition optimization in rotary kiln

Efficient recovery of zinc and copper from copper smelting slag (CSS) by cooperative modification with a composite medium of FeS-O2

Efficient Recycling of Silver and Copper from Sintering Dust by Chlorination Roasting Process

Recovery of Zinc and Silver from Zinc Acid-Leaching Residue by Sulphation Roasting-Water Leaching of Zinc and Iron-Silver Chlorination Leaching Method

Study on the Removal of Chloride Ions in an Acidic Solution of Zinc Smelting by Green Method

Pyrometallurgical Recovery of Valuable Metals from Flue Dusts of Copper Smelter Through Lead Alloy

Stepwise recovery of Ni, Cu, Zn, and Cr: A green route to resourceful disposal of electroplating sludge

Extraction of Lead and Zinc from a Rotary Kiln Oxidizing Roasting Cinder