Experimental and Mechanism Research on Vacuum Carbothermal Reduction of Zinc-Containing Electric Arc Furnace Dust
Xuan He,Shufang Xie,Xianfen Li,Xiaodong Lv,Run Huang
DOI: https://doi.org/10.1007/s11837-022-05375-0
2022-06-28
JOM
Abstract:The vacuum carbothermal reduction of Zn electric arc furnace dust (EAFD) was investigated using x-ray diffraction, SEM imaging, EDS-mapping, x-ray photoelectron spectroscopy, thermogravimetric analysis, and chemical titration. In vacuum, 96.29% of Zn in EAFD was reduced and volatilized, and the maximum mass loss of EAFD occurred at 1000°C, which was lower than that in argon. In vacuum, the reduction of ZnFe2O4 to Fe3O4 and ZnO was initiated at 700°C. As the temperature increased from 700°C to 800°C, the reduction of Fe3O4 to FeO was initiated, whereas K salts in EAFD were completely volatilized and accumulated in a condenser. At 850°C, ZnFe2O4 and Fe3O4 were completely reduced, and the reduction of FeO and ZnO was initiated. At 1000°C, ZnO and FeO were completely reduced, and Zn was volatilized and accumulated in a condenser, whereas metal Fe remained in the slag to form a Fe-rich slag.
materials science, multidisciplinary,metallurgy & metallurgical engineering,mining & mineral processing,mineralogy