EFFECT OF SURFACE ROUGHNESS ON VERY HIGH CYCLE FATIGUE BEHAVIOR OF Ti-6Al-4V ALLOY

Zhu Lina,Deng Caiyan,Wang Dongpo,Hu Shengsun

DOI: https://doi.org/10.11900/0412.1961.2015.00511

IF: 1.797

2016-01-01

ACTA METALLURGICA SINICA

Abstract:Ti-6Al-4V alloys are widely used in aero engine blades for their unique properties, such as high specific strength, high specific stiffness and high fatigue strength. Aero engine blades usually suffer a variety of cyclic loading during the period of services, which finally results in fatigue failure. Fatigue life of materials is known to highly depend on the surface quality. Consequently, more and more researches about the influence of machined surface roughness on the fatigue behavior of materials have been carried out in the last decades. However, there are less relevant results about the relationship between surface roughness and very high cycle fatigue (VHCF) properties of Ti-6Al-4V alloy. To investigate the effects of surface roughness on fatigue properties of Ti-6Al-4V alloy under very high cycle fatigue regimes, ultrasonic fatigue tests were conducted at the conditions of 20 kHz and stress ratio R-1=-1 at room temperature in air. During ultrasonic fatigue testing, each specimen was water-cooled. The specimen surfaces were cut and grinded which gave different surface roughnesses. The surface roughness was characterized using profilometry. In order to explain the high dependence of stress-fatigue life curves on the surface roughness, an approach based on the finite element analysis of measured surface topography was proposed. The results show that the VHCF property of Ti-6Al-4V alloy was significantly affected by surface roughness. The critical flaw size was 0.49 similar to 1.10 mu m when the ratio between spacing and height of circumferential grooves was between 2 similar to 10. When surface roughness was smaller than the critical flaw size, surface roughness exerted no influence on fatigue life. While surface roughness was greater than critical flaw size, fatigue life decreased with increasing surface roughness. Surface roughness played a more important role in long life regime than that in VHCF regime in which with the growth of surface roughness, the crack initiation site changed from single one to two or more ones, as well as changed from inside to subsurface. When the surface roughness was large enough, all cracks initiated from surface even in super long life regime.