Abstract:Purpose The majority of machine component failures are caused by load conditions that change with time. Under those circumstances, the component can function effectively for a long time but then breaks down unexpectedly and without warning. Therefore, the study of fatigue considerations in design becomes important. Also, to determine the component's long-term tenability, fatigue behavior must be investigated. This paper aims to investigate the fatigue life of aluminum 6061-T6 alloy under uniaxial loading using experiments and finite element simulation. Design/methodology/approach Both base metal (BM) and friction stir welding (FSW) configurations have been used to analyze fatigue behavior. The experimental tests were carried out using Instron-8801 hydraulic fatigue testing machine at frequency of 20 Hz and load ratio of 0.1. The yield strength, ultimate tensile strength, amplitude stress and fatigue life were used as input in simulation analysis software. Based on the findings of the tensile test, the maximum stress applied during the fatigue testing was estimated. Simulated and experimental results were also used to plot and validate the S-N curves. The fracture behavior of specimens was also examined using fractographic analysis. Findings The fractured surfaces indicate both brittle and ductile failure in the specimens. However, dimples dominated during the final fracture. The comparison between experimental and simulation results illustrates that the difference in fatigue cycles increases with an increase in the yield strength of both BM and FSWed specimens. This disparity is attributed to many factors such as scratches, rough surfaces and microstructural behavior. Aluminum 6061-T6 alloy is considered a noteworthy material where high strength with reduced weight contributes to the crash-worthy design of automobile structures. Originality/value The current study is significant in the prediction of the fatigue life of aluminum 6061-T6 alloy using experiments and simulation analysis. A good correlation was found when the experimental and simulation analysis were compared. The proposed simulation analysis approach can be used to anticipate a component's fatigue life.

An Evaluation on High Cycle Fatigue Fracture Characteristics of 2024-T351 Al Alloy with Different Surface Defects

Fatigue Damage Behavior and Mechanism Research of 2198 Aluminum–Lithium Alloy Sheet with Error Holes

Study on Fatigue Life of Aluminum Alloy 6061-T6 Based on Random Defect Characteristics

Fatigue life analysis for 6061-T6 aluminum alloy based on surface roughness

Role of defects on the high cycle fatigue behavior of selective laser melted Al–Mg–Sc–Zr alloy

Fatigue life prediction of aluminum alloy 6061 based on defects analysis

High-Cycle Fatigue Performance of Laser Powder Bed Fusion Ti-6Al-4V Alloy with Inherent Internal Defects: A Critical Literature Review

Experimental and simulation analysis of fatigue life of aluminum 6061-T6 alloy

Fatigue tests and damage model development on Al-Si-Mg aluminum alloys with low-velocity impact pit

CHARACTERIZATION OF SURFACE, SUBSURFACE DAMAGE AND THEIR EFFECT ON FATIGUE LIFE AFTER MACHINING OF AEROSPACE-GRADE ALUMINUM ALLOY (Al 6082-T6)

Characterization of Surface Fatigue Crack Nucleation and Microstructurally Small Crack Growth in High Strength Aluminum Alloys

Effect of Pre-fatigue Damage on the Residual Strength of 2198-T8 Aluminum-Lithium Alloy Sheet with Holes

An Approach for Predicting the Low-Cycle-Fatigue Crack Initiation Life of Ultrafine-Grained Aluminum Alloy Considering Inhomogeneous Deformation and Microscale Multiaxial Strain

Notches and Fatigue on Aircraft-Grade Aluminium Alloys

Fatigue tests and a damage mechanics-based fatigue model on a cast Al-Si-Mg aluminum alloy with scratches

Ductile Fracture and S–N Curve Simulation of a 7075-T6 Aluminum Alloy under Static and Constant Low-Cycle Fatigue

A Study on the Corrosion Fatigue Characteristics of Al 2024-T3 Alloy

Failure Mechanism Research on Bending Fretting Fatigue of 6061-T6 Aluminum Alloy by Experiment and Finite Element Method

Test Studies on Fatigue Performance of Aluminum Alloys Used in Construction

The effect of defect population on the anisotropic fatigue resistance of AlSi10Mg alloy fabricated by laser powder bed fusion

New ultra-low cycle fatigue model for metal alloys