Abstract:TiAl-based alloys have recently received considerable attention as one of the promising candidates for application in aero engine blades by replacing the Ni-based superalloys because of their unique properties, such as high specific strength, high specific stiffness and good oxidation resistance. However, there are some shortcomings limiting the application of TiAl-based alloys, namely, their brittleness and poor processing properties. Nevertheless, aero engine blades usually suffer a variety of cyclic loadings during the period of services, which finally results in fatigue failure. According to statistics, fatigue failure, mainly high cycle fatigue (HCF), occupies almost 80% failure modes of gas turbine blades in aero engines. Consequently, more and more researches about fatigue behavior of blade materials have been done in the last tens of years. However, there are less relevant results about TiAl-based alloys, especially HCF properties. Recently, the advancement of directional solidification (DS) of TiAl-based alloys using cold crucible has revealed that the ductility can be enhanced at room and elevated temperature. For purpose to verify the influence of DS structures on the tensile and HCF properties, TiAl-based alloy in composition with Ti-47Al-2Cr-2Nb (atomic fraction, %) was prepared and evaluated in this work. Directionally solidified Ti-47Al-2Cr-2Nb alloy ingots with different withdrawal rates (1.0, 1.2 and 1.4 mm/min) were prepared by cold crucible method under alter electromagnetic field in a vacuum furnace. Based on these ingots, macro and microstructures have been characterized by methods of digital camera, OM, SEM and XRD. Furthermore, the tensile properties at room and high temperature (800 degrees C) as well as HCF properties at room temperature have been measured respectively. So, the relationship between microstructures and mechanical properties of TiAl-based alloy, especially HCF properties, was demonstrated reasonably and mechanism in which HCF cracks propagated was discussed. The results show that the comprehensive mechanical properties of Ti-47Al-2Cr-2Nb alloy can be significantly improved after directionally solidified using cold crucible. The tensile strength reaches 652 MPa at room temperature with the maximum elongation of 1.5%. Meanwhile, the tensile strength at 800 degrees C attains 490 MPa with the elongation of 5.0%. Based on the data of HCF test at room temperature with the stress ratio of 0.1, the equations of stress amplitude-number of cycles to failure (S-N) curve at different withdrawal rates are calculated. The fatigue limits are 300 and 247 MPa with the withdrawal rates of 1.0 and 1.2 mm/min, respectively, namely, with the increase of withdrawal rate, the fatigue fracture resistance decreases. The mode of HCF fracture of directionally solidified Ti-47Al-2Cr-2Nb alloy behaves in brittle cleavage fracture. And micro-cracks which can propagate along and perpendicular to the lamellae at the same time are observed between alpha(2)/gamma lamellae and around B-2 phases.

Influence of the volume content of α + β colonies on the very high cycle fatigue behavior of a titanium alloy

Microstructural effects on the high-cycle fatigue and fracture behaviors of Ti-6Al-4V alloy

Effect of Size of Alpha Phases on Cyclic Deformation and Fatigue Crack Initiation During Fatigue of an Alpha-Beta Titanium Alloy

Fatigue property and failure mechanism of TC4 titanium alloy in the HCF and VHCF region considering different forging processes

Effect Of Microstructure On The High-Cycle Fatigue Behavior Of Ti(43-44)Al4nb1mo (Tnm) Alloys

TENSILE AND HIGH CYCLE FATIGUE PROPERTIES OF Ti-47Al-2Cr-2Nb DIRECTIONALLY SOLIDIFIED BY COLD CRUCIBLE METHOD

The Effect of Microstructure on the Very High Cycle Fatigue Behavior of Ti-6Al-4V Alloy

Effect of Heat Treatment on Very High Cycle Fatigue Properties of TC4

Rotation Bending High Cycle Fatigue Behaviors of TC21 Alloy with Bimodal Microstructure

The mechanism of internal fatigue-crack initiation and early growth in a titanium alloy with lamellar and equiaxed microstructure

High-cycle Fatigue of a Titanium Alloy: the Role of Microstructure in Slip Irreversibility and Crack Initiation

High cycle fatigue behavior of titanium microalloyed high-strength beam steels

Remarkable increase in high-cycle fatigue resistance in a titanium alloy with a fully lamellar microstructure

Characteristic and mechanism of crack initiation and early growth of an additively manufactured Ti-6Al-4V in very high cycle fatigue regime

Investigation of fatigue behavior of laser powder bed fusion Ti-6Al-4V: Roles of heat treatment and microstructure

Fatigue Crack-Initiation Mechanisms of a Dual-Phase Titanium Alloy Exhibiting High Tensile and High-Cycle Fatigue Properties

The Effect of Microstructure and Axial Tension on Three-Point Bending Fatigue Behavior of TC4 in High Cycle and Very High Cycle Regimes

Effect of Microstructure on Ultra-High Cycle Fatigue Behavior of Ti–6Al–4V

Titanium Alloy Materials with Very High Cycle Fatigue: A Review

Fatigue behavior of H-6A1-4V alloy in very high cycle regime

Stress Ratio and Notch Effects on the Very High Cycle Fatigue Properties of a Near-Alpha Titanium Alloy