Abstract:27Al and 29Si solid-state NMR spectra and X-ray diffraction (XRD) patterns were obtained for α-SiAlON powders prepared by combustion synthesis, according to which the phase transformation and structure evolution of α-SiAlON were studied. It was found that in α-SiAlON 29Si chemical shift values (−48<δSi<−47) were close to those in β-Si3N4 and α-Si3N4, indicating that Si atoms kept SiN4 coordination to a large extent in α-SiAlON despite the presence of O atoms. Dissimilarly, 27Al chemical shift values in α-SiAlON deviated clearly from that corresponding to AlN4 coordination (δAl∼112) and occurred in a range from δAl 95.5 to 99.9, which should be assigned to tetrahedral AlOxN4−x (0≤x≤4) coordination. The broadening effect of AlOxN4−x peaks was noticed, which was suggested to induced by slight dispersion of α-SiAlON compositions. 27Al resonances assigned to AlO4 or AlO6 were also observed, revealing the existence of glassy phase in combustion products. By comparing the intensities of AlO4 and AlO6 resonance peaks, it was found that the composition and structure of the co-existing liquid assisting α-SiAlON formation were not constant but varied with temperature in combustion synthesis. In addition, with CaF2 used as Ca-source α-SiAlON with low oxygen contents (n<m/2) were prepared, and it was found that there was a low threshold of oxygen content only beyond which α-SiAlON could be formed.

Combustion synthesis of alpha SiAlON powders with low oxygen contents by using fluorides as reactants

Combustion Synthesis of α-SiAlON Powders with Low Oxygen Contents by Using Fluorides as Reactants

Solid-state NMR and XRD study of α-SiAlON powders prepared by combustion synthesis

Oxidation of Ca-α-SiAlON Powders Prepared by Combustion Synthesis

Combustion synthesis of α-Si3N4 powders using in-situ nano-SiO2 coated Si and Si3N4 reactants

Fabrication of yttrium-stabilized α -SiAlON powders with rod-like crystals by combustion synthesis

Oxidation Behavior of Β-Sialon Powders Fabricated by Combustion Synthesis

Fabrication of one-dimensional rod-like α-SiAlON powders in large scales by combustion synthesis

Phase transformation and growth of rod-like α-SiAlON particles during combustion synthesis

Mechanical-activation-assisted combustion synthesis of α-SiAlON in air

Effect of Nitrogen Pressure and Additives on Combustion Synthesis of Rod-Like Yttrium α-SiAlON Crystals

Effects of starting compositions on the phase composition and microstructure of Yb α-SiAlON prepared by combustion synthesis

Preparation of Ca α-SiAlON powders with rod-like crystals by combustion synthesis

Controllable Synthesis of High-purity β-SiAlON Powder

Preparation, Oxidation Property and Mechanism of Si3N4/O′-SiAlON Composite Ceramics

Controllable Synthesis of High-purity β-SiAlON Powder: Controllable Synthesis of High-purity β-SiAlON Powder

Combustion Synthesis of β-Si<sub>3</sub>N<sub>4</sub> and β-SiAlON with Elongated Prismatic Micro-Crystals by Adding SrCO<sub>3</sub> and NH<sub>4</sub>F

Sintering Behavior, Microstructure and Mechanical Properties of Various Fluorine-Containing Y-SiAlON Glass-Ceramics

Preparation of Y-SiAlON rod-like crystals and whiskers by combustion synthesis

Rapid synthesis of AlON powders by nitriding combustion synthesis precursor

Combustion Synthesis Of Beta-Si3n4 And Beta-Sialon With Elongated Prismatic Micro-Crystals By Adding Srco3 And Nh4f