Mechanical and corrosion properties of thin Hastelloy C-276 plate by pulsed laser welding with filler wire

Guangyi Ma,Dongjiang Wu,Dongdong Wu,Mingkai Lei
2017-01-01
Abstract:To meet the special requirements of Hastelloy C-276 welding in extreme environment, tensile tests and electrochemical corrosion tests of thin Hastelloy C-276 plate by pulsed laser welding with filler wire (LWFW) were carried out. Laser scanning confocal microscope (LSCM) and Energy Dispersive X-ray Spectrometry analysis (EDS) were carried out to study the corrosion mechanisms and the corroded surface element distribution features. The results indicated, the tensile strength of welding joint with a certain positive reinforcement was higher than that of base metal. Also, all tensile tests were broken at the base metal. In the neutral solution, the corrosion resistance of the weld was greater than that of the base metal. However, in the weak acidic solution, the corrosion resistance of the weld and base metal were similar. In both solutions, the intergranular corrosion occurred at the weld, selective corrosion at the base metal, and a Mo-rich passivation film was grown on the surface of the weaker corroded region.
What problem does this paper attempt to address?