Effect of Fe-based metallic glass on microstructure and properties of Hastelloy X manufactured by laser powder bed fusion
Guojie Liu,Bolin Li,Shuai Zhang,Jiyuan Liu,Hao Ying,Dong Li,Chuqi Xie,Xinyi Zhang,Li Wang,Yong Liu,Shenghai Wang
DOI: https://doi.org/10.1016/j.jallcom.2023.171561
IF: 6.2
2023-08-02
Journal of Alloys and Compounds
Abstract:Hastelloy X is widely used in aerospace because of its excellent high-temperature performance. Laser powder bed fusion (LPBF) can be used to manufacture Hastelloy X and its reinforced materials with more complex structures and better performance. In this study, Hastelloy X reinforced materials added Fe-based metallic glass powder was manufactured using LPBF, and four sequences of 0, 3, 5, and 7 wt%. The introduction of Fe-based metallic glass powder has exhibited notable improvements in the mechanical properties at room and high temperatures. At room temperature (RT), the 5 wt% reinforced material exhibited a larger increase in hardness, with a yield strength and ultimate tensile strength of 856Mpa and 1081 MPa, and the reduction in elongation was only 9.6%. At high temperatures, introducing Fe-based metallic glass enhanced the yield strength and ultimate tensile strength, and the elongation was greatly improved at 800 °C. The enhancements are mainly due to the grain size refinement caused by the introduction of Fe-based metallic glass powder, which increases dislocation density and grain boundary strengthening. In addition, as the content of Fe-based metallic glass increased, the corrosion resistance of the samples was also improved due to increased Cr and W content and the refinement of grains. This study provides a new research direction for improving the properties of Hastelloy X.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering