Microstructure and Tensile Properties of Microwave Welded Hastelloy C-276 Joints

Kadapa Vijaya Bhaskar Reddy,Gudipadu Venkatesh,Radha Raman Mishra
DOI: https://doi.org/10.1007/s11665-024-09576-3
IF: 2.3
2024-05-22
Journal of Materials Engineering and Performance
Abstract:In this paper, microwave joining of Hastelloy C-276 joints is reported using Hastelloy C-276 powder as an interlayer (~ 15 ± 6 μm). Microwave hybrid heating technique was adopted to develop the joints using a graphite susceptor inside a multimode microwave applicator at 900 W power, frequency of 2.45 GHz and 760 s exposure time. The joints were characterized to study the microstructure, hardness, and tensile properties. Microstructural analysis revealed defect and crack-free joints with adequate metallurgical bonding and diffusion between interface layer and base material. Fine cellular (spherical) microstructure and skeleton-like hard carbides were present at the grain boundaries. Formation of intermetallic phases Fe 3 Ni and Ni 3 Cr was confirmed by the XRD analysis, whereas hard carbides Mo 2 C and W 2 C were identified by EDS analysis. The welded zone possesses 23% higher microhardness than base metal with an average microhardness of 282 HV. The ultimate tensile strength of the joint was estimated 602 ± 22 MPa with 20% of elongation capacity, and the achieved joint efficiency was 82%. Fractography analysis reveals the failure of the joint due to mixed (shear, ductile, and brittle) modes.
materials science, multidisciplinary
What problem does this paper attempt to address?