Structural , thermal and microwave dielectric properties of a novel microwave material Ba 2 TiGe

Huaicheng Xiang,Yang Bai,Chunchun Li,Liang Fang,Heli Jantunen

2018-01-01

Abstract:Rapid development of the microwave dielectric materials have emerged in recent * Corresponding author. E-mail addresses: xianghuaicheng@126.com, Huaicheng.Xiang@oulu.fi (H. Xiang); fanglianggl001@aliyun.com (L. Fang) 2 years due to their wide applications and revolution in the wireless communications. However, many commercial microwave materials are based on titanates, niobates and tantalates which have disadvantages of costly raw materials and significantly high sintering temperatures (not energy efficient). In this paper, we develop a BaO-TiO2GeO2 ternary system from the BaO-TiO2 binary system, in order to obtain low temperature co-fired microwave dielectric ceramics for high frequency applications. Ba2TiGe2O8 ceramics were prepared via the conventional solid-state route. The X-ray diffraction results show that the Ba2TiGe2O8 belongs to the orthorhombic, Cmm2 space group. The Ba2TiGe2O8 ceramics exhibit a densification of 96.3% after being sintered at 1060 °C. They also exhibit relative permittivity (r) of 12.7, quality factor (Q×f) of 9,060 (at 10 GHz), temperature coefficient of resonant frequency (f) of –30 ppm/°C and coefficient of thermal expansion (CTE) of 11.0 ppm/°C. In addition, the Raman spectra, ionic polarizability, packing fraction and bond valence of Ba2TiGe2O8 unit cells are investigated.