Abstract:Engineered cementitious composites (ECC) are a class of high‐performing fibre‐reinforced cementitious materials recognised for their increased ductility and durability compared to conventional cement‐based materials, owing to their autogenously controlled tight crack widths, even when subjected to high strains. To reduce ECC's environmental impact, this research examines the use of a low‐clinker binder − limestone‐calcined clay cement (LC3) − as an alternative to portland cement (PC), along with fly ash to further reduce the clinker proportion and the embodied CO2 of the formulations. In conventional concrete, LC3 hydrates to a denser microstructure resulting from the synergistic reaction between limestone and calcined clay. At the lower water contents typical of ECC and with the presence of fly ash, the influence of the binder composition on the microstructure is difficult to anticipate. To examine the influence of these compositional variables on microstructure, permeability and durability, the sulphate resistance of LC3‐based ECC is explored. Specifically, the ECC‐LC3 blends are designed with high clinker replacement rate of 75% by mass of binder and contain either conventional fly ash or reclaimed fly ash at 50% by mass of binder. Expansion of ECC‐LC3 samples subjected to standard sodium sulphate test conditions was measured up to 12 months and the depth of penetration of sulphates into the ECC‐LC3 of varying compositions was quantified using micro‐X‐Ray Fluorescence (microXRF) imaging and modelling. The expansion results show that the ECC‐LC3 formulations performed better than the PC samples and can provide adequate resistance to external sulphate attack, even when reclaimed fly ashes are used in place of the conventional ash. In addition, the shallow penetration of sulphate into these cementitious composites demonstrates the low diffusion coefficients values that were determined using the quantitative data from MicroXRF imaging.

Chloride Ion Permeability of Low Shrinkage Engineered Cementitious Composite

Experimental Study on Chloride Penetration in Cracked Engineered Cementitious Composite under Soak-Dry Cycles

Evaluation of shrinkage induced cracking performance of low shrinkage engineered cementitious composite by ring tests

Mapping of cracking sequence of polyvinyl alcohol-steel hybrid fiber reinforced high-strength engineered cementitious composite under uniaxial tension

Development of cementitious capillary crystalline waterproofing agents and durability study of concrete in the presence of chloride with sulfate in aqueous environment

Experiments of chloride ingression in flexural reinforced concrete beams

Chloride Penetrating under Co-Effects of Initial Curing and Exposure Conditions

Comparative Study on Clˉ Penetration in Cracked High Ductility and Low Shrinkage Material and Steel Fiber Concrete

Chloride Permeability in Cement-Based Materials Based on DC/AC Methods

Effects of controlled permeability formwork on surface properties and early age shrinkage of concrete

Chloride Ingress in Internally Cured Concrete under Complex Solution

Cracking Load of High Strength ECC-steel Composite Bridge Deck with Impact of Shrinkage Stress—test and Simulation

The Influence of Fly Ash on the Bending Characteristics of Cost-Effective Cementitious Composites

Mechanical Performance of Low Shrinkage Engineered Cementitious Composite in Tension and Compression

Engineered Cementitious Composite with Characteristic of Low Drying Shrinkage

Chloride penetration in concrete exposed to cyclic drying-wetting and carbonation

Bending Performance of Low Shrinkage Engineered Cementitious Composites-Concrete Composite Beam:Simulation and Validation

Sulphate resistance of low‐clinker engineered cementitious composites examined by MicroXRF imaging

Tensile Properties of Low Shrinkage Engineered Cementitious Composite

Chloride ion permeability of Ultra-high-performance fiber-reinforced concrete under sustained load

Engineered cementitious composites using blended limestone calcined clay and fly ash: Mechanical properties and drying shrinkage modeling