Crack Propagation Path Selection and Plastic Deformation at a Crack Tip in Zirconium

Zhouyao Wang,Qingshan Dong,Ning Guo,Mark R. Daymond
DOI: https://doi.org/10.1016/j.msea.2020.139143
IF: 6.044
2020-01-01
Materials Science and Engineering A
Abstract:The crack propagation process of a center cracked tension specimen was studied in pure zirconium by quasi-in-situ microstructure characterization combined with finite element modeling (FEM). The microstructure characterization shows that as load increased, dislocations were emitted from crack-tip ledges and crystallographic planes were 'thinned' by accumulation of slip traces at the crack-tip. In the near-crack region, plastic deformation was achieved mainly through dislocation motion, rather than twinning. It was observed that the crack grew along grains with plastically 'hard' orientations (as determined by the angle between c-axis and loading axis) and that cleavage fracture planes were found to be non-basal. In addition, combined with the crack-tip stress field from a simulation, the Schmid factor was estimated for prismatic, basal and pyramidal slip systems at the crack tip; the results were compared with experimental determinations of geometrically necessary dislocation density. It was found that the existence of the crack-tip stress field slightly suppressed prismatic and pyramidal slip as compared to that determined by a far-field stress state Schmid factor analysis.
What problem does this paper attempt to address?