Abstract:This study investigated the effect of layered double hydroxides (LDHs) on the deterioration process of cement paste in the sulfate environment. Cement pastes with the addition of original and calcined LDHs at 2.5 wt.% and 5.0 wt.% of cement were exposed to Na2SO4 solution for 360 days. The macroscopic performance of the cement paste was assessed based on mass variation, porosity, compressive strength, and content of sulfate ions. Furthermore, the microhardness, microstructures, and composition of the degraded pastes were examined using Vickers hardness (HV), mercury intrusion porosimetry (MIP), scanning electron microscope (SEM), X-ray diffraction (XRD), and thermogravimetric analysis (TGA). The results indicate that cement paste incorporated with LDHs can mitigate the corrosion caused by sulfate effectively, especially in the case of calcined LDHs (C-LDHs), which primarily increase the adsorption of sulfate. Compared with the control specimen, the 180 d compressive strength loss ratio of specimens with 2.5 wt.% and 5.0 wt.% of C-LDHs decreased by 63.66% and 80.51%, respectively. Moreover, LDHs can reduce the amount of ettringite crystals, densify the microstructure, and refine the pore structure to mitigate the cement paste's sulfate corrosion significantly. Compared with the control specimen, the 180 d harmful pore volume fraction of specimens laced with 2.5 wt.% and 5.0 wt.% C-LDHs decreased by 43.77% and 54.51%, respectively. In terms of the content of C-LDHs, an optimal content of C-LDHs could ensure the dominant effect of adsorption, while excessive C-LDHs could refine pores. In addition, Vickers hardness has an excellent correlation with compressive strength, which could precisely predict the compressive strength. Moreover, by combining the Vickers hardness distribution and content distribution of sulfate ions, the cross-section of the paste could be classified into four regions to evaluate the deterioration process accurately: the degraded zone, the strengthened zone, the invaded zone, and the intact zone.

A Comparable Study on the Deterioration of Limestone Powder Blended Cement under Sodium Sulfate and Magnesium Sulfate Attack at a Low Temperature

Form and mechanism of sulfate attack on cement-based material made of limestone powder at low water-binder ratio under low temperature conditions

Effect of environmental pH values on phase composition and microstructure of Portland cement paste under sulfate attack

Effect of Layered Double Hydroxides on the Deterioration Process of Cement Paste under Sulfate Attack

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Study on the Stability of Low-Carbon Magnesium Cementitious Materials in Sulfate Erosion Environments

Properties evolution of calcium sulfoaluminate cement blended with ground granulated blast furnace slag suffered from sulfate attack

Evaluation of Sulfate Resistance of Calcined Dolomite Activated Ground Granulated Blast Furnace Slag

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Contradict mechanism of long-term magnesium and sodium sulfate attacks of nano silica-modified cement mortars – Experimental and thermodynamic modeling

Effects of Sulfate and Magnesium on Cement Degradation under Geologic CO2 Sequestration Conditions

The Role of Limestone Powder in the Corrosion Products of Cement Mortars under Magnesium Sulfate Solution

Degradation characteristics of Portland cement mortar incorporating supplementary cementitious materials under multi-ions attacks and drying-wetting cycles

Impact of Leaching and Chlorides on Sulfate Attack for Cement Paste

Effect of an Early-Age Exposure on the Degradation Mechanisms of Cement Paste under External Sulfate Attack

Research on Sulfate Attack Mechanism of Cement Concrete Based on Chemical Thermodynamics

Investigating the sulfate resistance of mortars with multiple mineral admixtures in ammonium-magnesium sulfate solution

Effects of pH on the nano/micro structure of calcium silicate hydrate (C-S-H) under sulfate attack

Durability of phosphogypsum-based supersulfated cement mortar against external attack by sodium and magnesium sulfate

Deterioration Mechanisms of Ultra-High-Performance Concrete Under Various Sulfuric Acid and Sulfate Attack Conditions

Relationship Between Microscopic Pore Structure and Strength of Cement-Based Materials with Low Water-Binder Ratio Under Sulfate Attack Environment