Enhancing the specific capacity and rate performance of MoS₂ nanomaterials <i>via</i> introducing subgrains at a hydrothermal temperature 160 C

Zhenggang Jia,Xuexi Zhang,Jing Zhong,He Tian,Yueping Xiong

DOI: https://doi.org/10.1016/j.jelechem.2019.113659

IF: 4.598

2020-01-01

Journal of Electroanalytical Chemistry

Abstract:Reversible specific capacity and rate performance are required for MoS2 nanomaterials as lithium-ion batteries (LIBs) anodes. Here we reported a novel MoS2 structure with nano-size subgrain microstructure and thus enhanced electrochemical performance produced by a low-temperature hydrothermal synthesis technique. Ammonia solution treatment was proved feasible to remove the S-2(2-) and MoO3 impurities from the composite produces. After purification of the MoS2 prepared at a temperature of 160 degrees C, the (002) interlayer spacing was similar to 0.69 nm. In addition, the MoS2 sheets consisted of nano-size subgrains, with Mo enrichment at grain boundaries. As a result, a reversible specific capacity of 826 mAh g(-1) at a current density of 0.1 A g(-1) and rate performance of 700 mAh g(-1) at 1 A g(-1) were achieved. This shows that high purity MoS2 nanomaterials prepared via ammonia solution may act as promising materials for high performance anodes. (C) 2019 Elsevier B.V. All rights reserved.