One-Pot Hydrothermal Synthesis and Electrochemical Performance of Subspheroidal Core–Shell Structure MoS2/C Composite as Anode Material for Lithium-Ion Batteries

Wei Liu,Dongsheng Fan,Wei Wang,Shenshen Yang,Yaozong Lu,Lingping Fu,Jingbo Zhang,Yang Wu

DOI: https://doi.org/10.3390/en17071678

IF: 3.2

2024-04-01

Energies

Abstract:Molybdenum disulfide (MoS2) is a promising anode material for lithium-ion batteries (LIBs) due to its distinctive graphene-like structure and high specific capacity. However, its commercial application is hindered by the severe volume expansion during lithiation/delithiation and poor conductivity. In this paper, we report a facile one-pot enhanced hydrothermal synthesis strategy to prepare high-performance MoS2/C composite materials. The results indicate that the as-prepared MoS2/C composite is a subspheroidal core–shell structure material, with uniform coating, good particle dispersion, and an average grain size of approximately 80 nm. The morphology of the composite remained unchanged even after annealing at 500 °C for 2 h. The addition of glucose can accelerate the nucleation and growth of MoS2, and higher hydrothermal temperatures can improve the product yield. The addition of PVP has little effect on the yield, but significantly reduces the particle size. The XPS analysis reveals that the MoO3 may be generated as an intermediate product during the hydrothermal process. The electrochemical test results show that the unannealed MoS2/C samples exhibit discharge-specific capacities of 705.2 mAh·g−1 and 625.7 mAh·g−1 after the first cycle and the 100th cycle, respectively, at a current density of 500 mA·g−1, with a capacity retention rate of 88.7%. In contrast, the specific capacity of the MoS2/C specimens after annealing at 500 °C for 2 h shows a tendency to decrease and then slowly increase during the cycles, and the discharge specific capacity is 582.3 mAh·g−1 after the 100th cycle, which is lower than that of the unheated sample. The impedance analysis reveals that the lithium-ion diffusion coefficient of the MoS2/C material without calcination is 2.11 × 10−18 cm·s−2, which is superior to that of the annealed MoS2/C and pristine MoS2 samples. This characteristic is favorable for lithiation/delithiation during the charge/discharge process.

energy & fuels

What problem does this paper attempt to address?

The paper aims to address the following issues:

1. **Volume Expansion and Conductivity Issues**: Molybdenum disulfide (MoS₂) as an anode material for lithium-ion batteries (LIBs) has a unique graphene-like structure and high specific capacity, but it suffers from severe volume expansion and poor conductivity during charge and discharge processes, limiting its commercial application.

2. **Limitations of Existing Modification Methods**: Current research on the modification of MoS₂ mainly focuses on composite materials such as graphene and carbon nanotubes. These materials have complex synthesis processes and high costs. Additionally, while pursuing fine morphology and nanocrystallization can improve electrochemical performance, it may also lead to decreased material stability and specific capacity.

To solve the above problems, researchers have proposed a simple one-pot enhanced hydrothermal synthesis strategy to prepare high-performance MoS₂/C composites. Through this method, they aim to obtain a sub-spherical core-shell structure material with uniform coating, good dispersion, and an average particle size of about 80 nanometers, which can maintain its morphology even after annealing at 500°C. Experimental results show that the non-annealed MoS₂/C sample achieves a discharge specific capacity of 705.2 mAh·g⁻¹ after the first cycle at a current density of 500 mA·g⁻¹, and still maintains 625.7 mAh·g⁻¹ after the 100th cycle, with a capacity retention rate of 88.7%, demonstrating excellent electrochemical performance.