Abstract:This study utilizes desalted and denitrated treated aluminum dross (TAD) as a raw material, along with kaolin and 10 ppi (pores per inch) polyurethane foam as a template. The slurry is converted into an aluminum dross green body with a three-dimensional network structure using the impregnation method. A three-dimensional network aluminum dross ceramic framework (TAD3D) is created at a sintering temperature of 1350 °C. The liquid 5A05 aluminum alloy at a temperature of 950 °C infiltrates into the voids of TAD3D through pressureless infiltration, resulting in TAD3D/5A05Al composite material with an interpenetrating phase composite (IPC) structure. The corrosion behavior of TAD3D/5A05 composite material in sodium chloride solution was examined using the salt spray test (NSS) method. The study shows that the pores of the TAD3D framework, produced by sintering aluminum dross as raw material, are approximately 10 ppi. The bonding between TAD3D and 5A05Al interfaces is dense, with strong interfacial adhesion. The NSS corrosion time ranged from 24 h to 360 h, during which the composite material underwent pitting corrosion, crevice corrosion and self-healing processes. Results from Potentiodynamic Polarization (PDP) and Electrochemical Impedance Spectroscopy (EIS) indicate that, as corrosion progresses, the Ecorr of TAD3D/5A05Al decreases from −0.718 V to −0.786 V, and Icorr decreases from 0.398 μA·cm−2 to 0.141 μA·cm−2. A dense oxide film forms on the surface of the composite material, increasing the anodic Tafel slope and decreasing the cathodic Tafel slope, thus slowing down the rates of cathodic and anodic reactions. Factors such as lower interface corrosion resistance or a relatively weak passivation film at the interface do not significantly diminish the corrosion resistance of TAD3D and 5A05Al. The corrosion resistance of the composite material initially decreases and then increases.

Corrosion Behavior of WC–10 Wt % Ni3Al Composite in Acidic Media

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Microstructure and Corrosion Behaviour of WC-Co Coating Fabricated by Plasma Arc Welding

Electrochemical corrosion behavior of hot-pressing sintered WC-Al2O3 composite in alkaline and acidic solutions

WC-(7-9)Ni-(1-2)Cr Hard Alloy Anticorrosion Performance Research

Influence of Ni and Cr on Anti-corrosion Performance of Tungsten Carbide Base Hard Alloy

DRY AND HOT CORROSION BEHAVIOUR OF Al-Ni-Co-x MWCNT COMPOSITES PROCESSED THROUGH POWDER METALLURGY

Comparison on the immersion corrosion and electrochemical corrosion resistance of WC–Al 2 O 3 composites and WC–Co cemented carbide in NaCl solution

Corrosion Behavior of Al-containing CoNiV Alloys

Comparison of electrochemical corrosion between coarse-grained and fine-grained WC-Al2O3 composites in acidic and alkaline solutions

Preparation and Corrosion Resistance of Ni-W-CF Composite Coating on P110 Steel

Corrosion Behavior of Ni-P-Nano-Al2o3 Composite Coating in the Presence of Anionic and Cationic Surfactants

Improved mechanical performance and electrochemical corrosion of WC-Al2O3 composite in NaCl solution by adding the TiC additives

The Influence of Co Content and Sintering Time in Al–Al9Co2–Al13Co4 Composites on Microstructure and Corrosion Performance in NaOH Environment

Effects of W addition on the Corrosion Behaviors of FeCoNiCrMn High Entropy Alloy Composites in the 3.5 wt.% NaCl solution

Investigation of electrochemical dissolution behavior of Ni(γ)/Ni3Al(γ') and Co(γ)/Co3Al(γ') superalloys in NaNO3 solution

Corrosion Behavior of 10 ppi TAD3D/5A05Al Composite in a Chloride Environment

Corrosion Behavior of Ni/NiCr/NiCrAlSi Composite Coating on Copper for Application as a Heat Exchanger in Sea Water

Evaluation of Corrosion Behaviour of Ni/Wc-Mos2 Composite Coatings Prepared by Jet Electrodeposition with Different Mos2 Doping Concentrations

Improved electrochemical corrosion resistance of hot-press sintered WC–Al2O3 composites with added TiC in alkaline solutions

The corrosion performance for ultrafine WC-12Co processed by heat treatments in different pH solution