Improved mechanical performance and electrochemical corrosion of WC-Al2O3 composite in NaCl solution by adding the TiC additives

Bin Han,Shigen Zhu,Weiwei Dong,Yunfeng Bai,Hao Ding,Yilan Luo,Ping Di

DOI: https://doi.org/10.1016/j.ijrmhm.2021.105566

IF: 4.804

2021-09-01

International Journal of Refractory Metals and Hard Materials

Abstract:In this study, 85-xWC-xTiC-15wt%Al2O3 (x = 0, 5, 10 and 20 wt%) composites were fabricated via hot pressing sintering technology. The influences of TiC additives on the mechanical performance and electrochemical behavior of WC-Al2O3 composite in NaCl solution were investigated. The mean size of WC grain showed a downward trend with the increase of TiC content. The relative density, hardness and fracture toughness of WC-based composites were improved by TiC additives. The maximum values of mechanical performance were obtained when TiC content was 10 wt%. Moreover, the research results indicated that TiC additives significantly increase the corrosion potential and decrease the corrosion current density in NaCl solution. When TiC content increased, the charge-change resistance (Rct) value presented an uptrend, and then decreased obviously when the TiC content reached 20 wt%. The XPS spectrum and SEM images proved that TiO2 passivation film was formed on the surface of WA15-10TiC composite. Therefore, it could be concluded that TiO2 passive film could inhibit further corrosion of the composite.

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to improve the mechanical properties and electrochemical corrosion behavior in NaCl solution of WC - Al₂O₃ composites by adding different contents of TiC additives. Specifically, the research aims to explore the effects of TiC additives on the relative density, hardness, fracture toughness and electrochemical properties such as corrosion potential, corrosion current density and charge transfer resistance of WC - Al₂O₃ composites. The study found that when the TiC content is 10 wt%, the mechanical properties of the composite reach the best; at the same time, the addition of TiC significantly increases the corrosion potential of the composite in NaCl solution and reduces the corrosion current density, indicating that TiC additives can effectively improve the corrosion resistance of WC - Al₂O₃ composites. In addition, the research also confirmed through XPS spectra and SEM images that a TiO₂ passive film is formed on the surface of the WC - Al₂O₃ - 10TiC composite, and this film can inhibit the further corrosion of the composite.