The Influence of Co Content and Sintering Time in Al–Al9Co2–Al13Co4 Composites on Microstructure and Corrosion Performance in NaOH Environment

Imane Bahaj,Najoua Labjar,Mohammed Kaddami,Mohamed Essahli,El Mostapha Lotfi,Abdelouahed Dahrouch,Souad El Hajjaji

DOI: https://doi.org/10.1007/s40735-022-00727-4

2022-10-31

Abstract:The electrochemical behavior of Al–Al 9 Co 2 –Al 13 Co 4 aluminum matrix composites for room temperature in (1 M) NaOH environment was studied. In this work, the impact of sintering time (4 h, 8 h, 24 h, 48 h, and 72 h) and cobalt content (0.5, 1, 3, and 5%at) on the corrosion performance of these composites was investigated. Electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization were used to study electrochemical corrosion. Raman spectroscopy was used to characterize the film surface of the composites; while scanning electron microscope (SEM) coupled with energy-dispersive X-ray spectroscopy (EDS) was used to evaluate the microstructure after polarization. Improvements in corrosion resistance were shown by adjusting the heat treatment settings. The Al-5% Co alloy treated after 48 h of sintering showed the greatest resistance. Corrosion and deteriorating were seen to occur preferentially on some phases. The nobility of the intermetallic compounds of the Al-Co binary system in terms of chemical composition and crystal structure is discussed.