The Effect of B and Si Additions on the Structural and Magnetic Behavior of Fe-Co-Ni Alloy Prepared by High-energy Mechanical Milling
N. Khitouni,R. Daly,L. Escoda,N. Llorca-Isern,J. J. Suñol,M. Dammak,M. Khitouni
DOI: https://doi.org/10.1007/s10948-020-05500-7
2020-05-15
Journal of Superconductivity and Novel Magnetism
Abstract:Nanocrystalline Fe50Co25Ni15X10 (X = Bamorphous, Bcrystalline, and Si) powdered alloys were prepared by mechanical alloying process. Morphological, microstructural, and structural characterizations of the powders milled several times were investigated by scanning electron microscopy and X-ray diffraction. The final crystallographic state strongly depends on the chemical composition and the grinding time; it can be single-phase or two-phase. The crystallite size reduction down the nanometer scale is accompanied by the introduction of high level of lattice strains. The dissolution of Co, Ni, B (amorphous and crystalline), and Si into the α-Fe lattice leads to the formation of highly disordered Fe-based solid solutions. Coercivity (Hc) and the saturation magnetization (Ms) of alloyed powders were measured at room temperature by a vibration sample magnetization. The magnetic measurements show a contrasting Ms and (Hc) in all alloy compositions. Conclusively, soft magnetic properties of nanocrystalline alloys are related to various factors such as metalloid addition, formed phases, and chemical compositions.
physics, condensed matter, applied