Abstract:The influence of the elemental composition of strip amorphous alloys Fe 80.0 Si 6.0 B 14.0 , Fe 78.5 Ni 1.0 Mo 0.5 Si 6.0 B 14.0 ; Fe 73.1 Cu 1.0 Nb 3.0 Si 15.5 B 7.4 ; Fe 51.7 Ni 21.7 Cr 6.2 Mo 0.6 V 1.5 Si 5.2 B 13.1 on corrosion resistance in 0.5 M aqueous solutions of NaCl, HCl, and KOH at T = (293 ± 1) K was investigated. The high corrosion resistance of Fe 51.7 Ni 21.7 Cr 6.2 Mo 0.6 V 1.5 Si 5.2 B 13.1 and Fe 73.1 Cu 1.0 Nb 3.0 Si 15.5 B 7.4 alloys in aggressive environments was established. Electrochemical parameters obtained both by the method of cyclic voltammetry and electrochemical impedance spectroscopy (EIS) indicate the formation of more durable surface layers in a 0.5 M potassium hydroxide aqueous solution on these alloys. The Cl – ions (especially at low pH) under their long-term action are the more aggressive oxidizers of amorphous alloys compared to OH – ions. During the passivation film formation in highly aggressive environments such alloy elements, which do not participate in this process, actively dissolve, and the main film-forming elements accumulate under the film, thus improving its protective properties.

The Influence of the Composition of Amorphous Alloys on Their Corrosion Resistance in Aggressive Environments of Different Nature