Abstract:FeCrMnxAlCu (x = 2.0, 1.5, 1.0, 0.5, and 0.0) high-entropy alloys (HEAs) were prepared using vacuum arc melting. The phase structure, microstructure, and element distribution of FeCrMnxAlCu (x = 2.0, 1.5, 1.0, 0.5, and 0.0) HEAs were analyzed using X-ray diffraction, scanning electron microscopy, and energy-dispersive spectroscopy. The corrosion resistance of the alloy in a NaOH solution was evaluated using a potentiodynamic polarization curve, electrochemical impedance spectroscopy, an immersion test, WLI, and X-ray photoelectron spectroscopy. The results showed that FeCrMnxAlCu HEAs are an FCC+BCC bi-phase mixed structure with typical dendrite and interdendrite structures. The corrosion test demonstrated that the HEAs presented a breakthrough characteristic of activation–passivation–passivation. With an increase in Mn content, the corrosion potential shifted first positively and then negatively, and the corrosion current first decreased and then increased. Among HEAs, the FeCrMn0.5AlCu HEA had the best electrochemical corrosion resistance. After corrosion, both oxide and hydroxide corrosion product films were formed on the surface, which reduced the ion diffusion rate, slowed down the corrosion process, and improved the corrosion resistance.
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to explore the influence of different manganese (Mn) contents on the corrosion behavior of FeCrMn xAlCu high - entropy alloys in sodium hydroxide (NaOH) solution. Specifically, the researchers prepared a series of FeCrMn xAlCu high - entropy alloys with different manganese contents (x = 2.0, 1.5, 1.0, 0.5, and 0.0) and systematically studied the corrosion behavior and mechanism of these alloys in 1 M NaOH solution by using a variety of electrochemical test methods (such as potentiodynamic polarization curves, electrochemical impedance spectroscopy, immersion tests, etc.) and material characterization techniques (such as X - ray diffraction, scanning electron microscopy, energy - dispersive spectroscopy, white - light interferometer, etc.).
### Main research contents:
1. **Preparation and characterization of alloys**:
- FeCrMn xAlCu high - entropy alloys with different manganese contents were prepared by vacuum arc melting method.
- The phase structure of the alloys was analyzed by X - ray diffraction (XRD), and the results showed that these alloys had a two - phase mixed structure of FCC and BCC.
- The microstructure and element distribution of the alloys were observed by scanning electron microscopy (SEM) and energy - dispersive spectroscopy (EDS), and it was found that the thickness and length of dendrites changed with the increase of manganese content.
2. **Electrochemical corrosion performance test**:
- The corrosion behavior of the alloys in 1 M NaOH solution was studied by potentiodynamic polarization curve test, and the results showed that all samples exhibited passivation characteristics, but the passive film would be destroyed within a certain potential range.
- The corrosion resistance of the alloys was further analyzed by electrochemical impedance spectroscopy (EIS) test, and the results indicated that the FeCrMn 0.5AlCu alloy had the highest charge - transfer resistance and the lowest corrosion rate.
3. **Immersion test**:
- An immersion test for 168 hours was carried out to evaluate the long - term corrosion behavior of the alloys in a strongly alkaline environment.
- After immersion, the surface morphology and corrosion products of the alloys were analyzed by white - light interferometer (WLI) and X - ray photoelectron spectroscopy (XPS), and it was found that the corrosion products were mainly composed of oxides and hydroxides, and these corrosion product layers could slow down ion diffusion and improve the corrosion resistance of the alloys.
### Research conclusions:
- With the increase of manganese content, the corrosion potential of FeCrMn xAlCu high - entropy alloys first shifts positively and then negatively, and the corrosion current first decreases and then increases.
- Among them, the FeCrMn 0.5AlCu alloy exhibits the best electrochemical corrosion performance, with the most positive self - corrosion potential (- 0.538 V), the lowest self - corrosion current density (3.045×10^-6 A/cm²), and the highest charge - transfer resistance (7158.3 Ω·cm²).
- Oxide and hydroxide corrosion product layers are formed on the surface of the corroded alloys, and these product layers slow down ion diffusion and improve the corrosion resistance of the alloys.
In short, this study aims to deeply understand the influence of different manganese contents on the corrosion behavior of FeCrMn xAlCu high - entropy alloys in a strongly alkaline environment, and provides important experimental data and theoretical basis for designing high - entropy alloys with excellent corrosion resistance.