Effect of Cr/Mo/W on the Thermal Stability of Γ/γ′ Coherent Microstructure in Ni-Based Superalloys
Fan Lihua,Li Jinlin,Sun Jiudong,Lv Mengtian,Wang Qing,Dong Chuang
DOI: https://doi.org/10.11900/0412.1961.2022.00064
IF: 1.797
2024-01-01
ACTA METALLURGICA SINICA
Abstract:In general, Ni-based superalloys exhibit high strength, good oxidation and corrosion resistance, and good creep-resistant properties at high temperatures (HTs) because of the coherent precipitation of cuboidal.' nanoparticles into a fcc-gamma matrix induced by co-alloying of multiple elements. The present work designed a series of Ni-based superalloys based on the cluster composition formula [Al-Ni-12](Al-1 (Ti, Nb, Ta)(0.5)(Cr, Mo, W)(1.5)), with S1-CM (Cr1.0Mo0.5), S2-CW (Cr1.0W0.5), and S3-CMW (Cr0.7Mo0.4W0.4), in which the amounts of Cr, Mo, and W were changed, whereas the contents of other elements were main-tained. In addition, the effect of Cr, Mo, and W variation on the thermal stability of gamma/gamma ' coherent microstructure at HT in these superalloys was investigated. Alloy ingots were prepared by arc melting under an argon atmosphere, solid solutionized at 1300 degrees C for 15 h, and then aged at 900 degrees C for up to 500 h. Microstructural characterization and mechanical properties of these alloys in different aged states were studied by XRD, SEM, EPMA, TEM, Vickers hardness testing, and compressive testing.Result showed that all these three alloys have a high volume fraction (f > 70%) of gamma ' particles uniformly distributed in the fcc-gamma matrix. In particular, the gamma ' particle shape is ellipsoidal in S1-CM and S2-CW alloys, whereas it is cuboidal in the S3CMW alloy primarily because the latter has a more negative gamma/gamma ' lattice misfit (delta = - 0.47%) than the former (delta = - 0.25% to - 0.33%). After aging for 500 h, the morphology of gamma ' particles in each alloy has no evident change, and all of the particles have a slow coarsening rate (K = 10-18 nm(3)/s), in which the S3CMW alloy exhibits the highest gamma/gamma ' microstructural stability (the coarsening rate of gamma ' particles being K = 10.02 nm(3)/s). Moreover, the amount of second-phase precipitation near the grain boundaries in the S3CMW alloy is less than that in the former two alloys. The microhardness test results showed that the microhardness of each alloy remains almost constant with aging time, thereby indicating the thermal stability of the coherent structure. In particular, the microhardness of the S3-CMW alloy is 397-418 HV, and the room-temperature compression yield strength is 818 MPa in the 200-h-aged state.