Role of Oxygen Vacancies on the Performance of LiMn2O4 Spinel Cathodes for Lithium-Ion Batteries
Jing Wang,Haiyang Xing,Wenqiang Hou,Youlong Xu
DOI: https://doi.org/10.1039/d3cp01729j
IF: 3.3
2023-06-20
Physical Chemistry Chemical Physics
Abstract:Oxygen vacancies, known as unavoidable existence in spinel LiMn2O4 material, play an essential factor in its physicochemical and electrochemical properties. However, the function mechanism of oxygen vacancies and its influence on electrochemical properties are poorly understood so far. Hence, we investigate the role of oxygen vacancies in the spinel LiMn2O4 material by controlling the annealing atmosphere. The relative amount of oxygen deficiency in the samples prepared under oxygen and air atmosphere are 0.098 and 0.112, respectively. Impressively, we designed using air-calcined LiMn2O4 annealing under a nitrogen atmosphere, and the relative amount oxygen deficiency of oxygen annealed increased from 0.112 to 0.196. However, the conductivity of the material changes from 2.39 to 10.3 mS m-1, but the ion diffusion coefficient is significantly reduced from ~10-12 to ~10-13 cm2 s−1, resulting in a decrease in the initial discharge capacity from 136.8 to 85.2 mAh g-1. In addition, we attempted to use the nitrogen-sample annealing again under oxygen, which can significantly reduce the conductivity (from 10.3 to 6.89 mS m-1), and the discharge capacity also increased by 40% of the original. Therefore, the mechanism of the interaction of the oxygen vacancies on the material electronic conductivity, lithium-ion diffusion coefficient and electrochemical properties, provides a basis for the objective treatment of oxygen vacancies in spinel structured materials.
chemistry, physical,physics, atomic, molecular & chemical