Abstract:The oxides LiMn2O4, LiFe0.75Zn0.25MnO4, and LiFe0.25Zn0.25Mn1.5O4, referred to as LMO, LFZMO 0.75–0.25, and LFZMO 0.25–0.25, were synthesized at 800 °C using ultrasound-assisted thermal decomposition of nitrates (UA-TDN). X-ray diffraction (XRD) analyses confirmed the spinel structure (Fd3m space group) for all materials. Raman spectroscopy validated the characteristic absorption bands of the spinel phase. Energy-dispersive spectroscopy (EDS) verified the uniform distribution of Fe, Zn, Mn, and O in all samples and proved the expected stoichiometry for the different oxides. Scanning electron microscopy (SEM) images showed irregular polyhedral agglomerates in the synthesized oxides, with grain sizes ranging from approximately 600 to 800 nm. Electrochemical characterization was performed under N2 and O2 atmospheres, revealing electron-withdrawing effects with increasing iron content in the oxide composition. LFZMO 0.75–0.25, with a higher iron content, displayed better performance than LMO and LFZMO 0.25–0.25 in terms of discharge capacity and cycling performance at various rates. The greater discharge capacity of LFZMO 0.75–0.25 (47 mA h g −1) was in line with the cyclic voltammetry findings, wherein lower energy (∆GLi + / Li 0 = 55.5 kJ mol−1) for lithium insertion correlated with an increased discharge capacity. Electrochemical Impedance Spectroscopy (EIS) was employed to determine diffusion constants, providing insights into Li+ insertion kinetics in the cathodic electrode and highlighting the significant influence of Zn and Fe incorporation on the lithium manganese oxide. Our findings are intriguing as the diffusion coefficient of DLi + in LFZMO 0.75–0.25 (2.3 ×10−12 cm2 S−1) surpasses that of LMO (8.5 ×10−14 cm2 S−1) and LFZMO 0.25–0.25 (9.4 ×10−18 cm2 S−1). This observation further elucidates the more positive formal potential for Li+ insertion in LFZMO 0.75–0.25.

Correlation of oxygen deficiency with discharge capacity at 3.2V for (LiMn)3O4−z

Oxygen Deficiency, a Key Factor in Controlling the Cycle Performance of Mn-spinel Cathode for Lithium-Ion Batteries

Electrochemical and Physicochemical Behaviors of Oxygen-Deficient Manganese Spinel

Rate-dependent Electrochemical Reaction Mechanism of Spinel Metal Oxide Anode Studied by in Situ TEM

Dependence of electrochemical properties of spinel LiMn2O4 on Li2CO3 with micro-flaky, micro-flower and nanorod morphologies

Studies on the LiMnO spinel system (obtained from melt-impregnation method) as positive electrodes for 4 V lithium batteries. Part III. Characterization of capacity and rechargeability

Preparation of Submicrocrystal LiMn2O4 Used Mn3O4 As Precursor and Its Electrochemical Performance for Lithium Ion Battery

Correlating Capacity Fading and Structural Changes in Li1 + y Mn2 − y O 4 − δ Spinel Cathode Materials: A Systematic Study on the Effects of Li/Mn Ratio and Oxygen Deficiency

Changes in Mn3+/Mn4+ Ratio, Resistance Values in Electrochemical Impedance Spectra, and Rate Capability with Increased Lithium Content in Spinel LixMn2O4

Sulfur-doped enhanced ZnMn 2 O 4 spinel for high-capacity zinc-ion batteries: Facilitating charge transfer

Role of Oxygen Vacancies on the Performance of LiMn2O4 Spinel Cathodes for Lithium-Ion Batteries

lectrochemical properties of spinel LiMn 2 O 4 on Li 2 CO 3 with micro-fl aky , micro-fl ower and nanorod morphologies †

Effects of metal-ion substitution on the structural, morphological, and electrochemical properties of LiFexZnyMn2−x-yO4 (x, y = 0.25 or 0.75)

Dependence of Battery Performance of Spinel Li{sub 1+x}mn{sub 2}o{sub 4} on the Preparation Method

Exploring Lithium-Cobalt-Nickel Oxide Spinel Electrodes for ≥3.5 V Li-Ion Cells.

Dependence of electrochemical properties of spinel LiMn<sub>2</sub>O<sub>4</sub> on Li<sub>2</sub>CO<sub>3</sub> with micro-flaky, micro-flower and nanorod morphologies

Synthesis Spinel Limn2o4 With Manganese Carbonate Prepared By Microemulsion Method

Modulating the Proton‐Conducting Lanes in Spinel ZnMn2O4 through Off‐Stoichiometry

Studies on LiMnO spinel system (obtained from melt-impregnation method) as a cathode for 4 V lithium batteries Part II. Optimum spinel from γ-MnOOH

Dependence of Battery Performance of Spinel Li1+XMn2O4 on the Preparation Method

Doping Effect of Cobalt,cerium and Magnesium to Spinel LiMn2O4 on Their Structures Character and Properties