Shixing Chen,Guanqi Liu,Feiting Yu,Lei Chen,Zhanguo Liu,Yudong Fu,Yujin Wang,Jingchuan Zhu
DOI: https://doi.org/10.1016/j.matchar.2021.111604
IF: 4.537
2022-01-01
Materials Characterization
Abstract:The practical applications of ZrC are restricted by its low fracture toughness and resistance to sintering densification. This study reports the in-situ precipitation behavior of (Zr,W)C solid solution precipitates induced by Ti. The (Zr0.7W0.3)C solid solution powder was prepared via carbothermic reduction using pressureless sintering at 2200 °C for 1 h. Varying quantities of TiH2 were reacted with the (Zr0.7W0.3)C matrix, to precipitate the second phase in-situ, via hot-pressing sintering (50 MPa) at 1600 °C for 1 h. When the content of TiH2 was 10 mol%, W and W2C were the second phases precipitated. As the TiH2 concentration increased, the precipitates converted into W2C and the (Ti,Zr)C solid solution. Furthermore, nano-scale dot-like W precipitates gradually increased inside the crystal grains of the (Zr,W,Ti)C matrix. The optimized comprehensive mechanical properties of (Zr,W,Ti)C-based multiphase ceramics were obtained by adding 40 mol% TiH2; the relative density was 99.7%, the Vickers hardness was 24.68 GPa, and the fracture toughness was 5.76 MPa·m1/2. The precipitates (of varying type and concentration) exhibited distinct toughening effects relative to the (Zr,W)C solid solution.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing