Improved Sintering Behavior and Microwave Dielectric Properties of SnO2-based Ceramics and Their LTCC Materials with Ultrawide Temperature Stability
Kang Du,Wei Zhu,Changzhi Yin,Jiaxing Fang,Gaocheng Zhang,Cai Zhou,Shengxiang Wang,Wen Lei
DOI: https://doi.org/10.1016/j.ceramint.2022.08.203
IF: 5.532
2022-01-01
Ceramics International
Abstract:Microwave dielectric ceramics with simple composition, a low permittivity (er), high quality factor (Q x f) and temperature stability, specifically in the ultrawide temperature range, are vital for millimetre-wave communi-cation. Hence, in this study, the improvements in sintering behavior and microwave dielectric properties of the SnO2 ceramic with a porous microstructure were investigated. The relative density of the Sn1-xTixO2 ceramic (65.1%) was improved to 98.8%, and the optimal sintering temperature of Sn1-xTixO2 ceramics reduced from 1525 degrees C to 1325 degrees C when Sn4+ was substituted with Ti4+. Furthermore, the er of Sn1-xTixO2 (0 <= x <= 1.0) ce-ramics increased gradually with the rise in x, which can be ascribed to the increase in ionic polarisability and rattling effects of (Sn1-xTix)4+. The intrinsic dielectric loss was mainly controlled by rc (Sn/Ti-O), and the negative rf of the SnO2 ceramic was optimised to near zero (x = 0.1) by the Ti4+ substitution for Sn4+. This study also explored the ideal microwave dielectric properties (er = 13.7, Q x f = 40,700 GHz at 9.9 GHz, and rf =-7.2 ppm/degrees C) of the Sn0.9Ti0.1O2 ceramic. Its optimal sintering temperature was decreased to 950 degrees C when the sin-tering aids (ZnO-B2O3 glass and LiF) were introduced. The Sn0.9Ti0.1O2-5 wt% LiF ceramic also exhibited excellent microwave dielectric properties (er = 12.8, Q x f = 23,000 GHz at 10.5 GHz, and rf=-17.1 ppm/degrees C). At the ultrawide temperature range (-150 degrees C to +125 degrees C), the re of the Sn0.9Ti0.1O2-5 wt% LiF ceramic was +13.3 ppm/degrees C, indicating excellent temperature stability. The good chemical compatibility of the Sn0.9Ti0.1O2-5 wt% LiF ceramic and the Ag electrode demonstrates their potential application for millimetre-wave communication.