Structural and Microwave Dielectric Properties of High-Permittivity Ca0.245Li0.325Nd0.395Ti1−xSnxO3 Ceramics

Guan Yeqing,Zhang Jinxian,Wang Fenglin,Li Wei,Mao Haijun,Liu Zhuofeng,Zhang Weijun,Chen Xingyu

DOI: https://doi.org/10.1007/s10854-022-09650-3

2023-01-01

Journal of Materials Science Materials in Electronics

Abstract:The Ca0.245Li0.325Nd0.395Ti1−xSnxO3 (x = 0–0.12) ceramics were prepared by the traditional solid-state reaction method. The effects of Sn4+ substitution for Ti4+ on the phase composition, microstructure, and microwave dielectric properties of Ca0.245Li0.325Nd0.395Ti1−xSnxO3 (CLNTSx) were investigated in this work. The X-ray diffraction results showed that the ceramics had a single orthorhombic perovskite structure when x = 0–0.09. However, a secondary phase SnO2 was observed with x > 0.09. The SEM micrographs indicated that the proper Sn4+ substitution for Ti4+ promoted the grain growth and homogenization. The analysis results of Raman spectroscopy revealed the correlation between vibration modes and microwave dielectric properties of CLNTSx ceramics with different Sn4+ contents. The degree of cation order was related to the full width at half maximum (FWHM) of the Raman spectrum, and a lower FWHM value indicates higher cationic order and Q × f0 value. The excellent microwave dielectric properties with εr = 98, Q × f0 = 3320 GHz, and τf = 2.6 ppm/°C were obtained in the ceramics with x = 0.09 sintered at 1350 °C for 4 h.