High-permittivity Microwave Dielectric Ceramics Based on (1 - X)(li1/2nd1/2)tio3–xcatio3

Weijun Zhang,Xingyu Chen,Aiqing Jia,Shuxin Bai

DOI: https://doi.org/10.1142/s0217979215400263

2015-01-01

Abstract:Microwave (MW) dielectric ceramics in (1 - x)( Li 1/2 Nd 1/2) TiO 3–x CaTiO 3 (0.2 ≤ x ≤ 0.8) composition were prepared through the conventional solid-state reaction. X-ray diffraction (XRD) analysis and scanning electron microscopy (SEM) combined with energy dispersive X-ray analysis (EDX) indicated that the matrix phase was a continuous solid solution with orthorhombic perovskite structure. A minor amount of secondary phase was detected only in the composition of x = 0.7 and 0.8. The (1 - x)( Li 1/2 Nd 1/2) TiO 3–x CaTiO 3 ceramics showed a very high permittivity of 118–153 and reasonable Q × f0 values of 2360–5930 GHz as x increased from 0.2 to 0.8. The temperature coefficient of resonant frequency (τf) of the samples increased with increasing x value and was approximately linearly proportional to εr. Bi 4 B 2 O 9 addition effectively tailored the τf of (1 - x)( Li 1/2 Nd 1/2) TiO 3–x CaTiO 3 ceramics to near zero at low temperature, and induced no degradation of Q × f0 value. The x = 0.3 composition with 20 wt .% Bi 4 B 2 O 9 addition sintered at 1050°C exhibited dielectric properties of εr = 112.4, Q × f0 = 2414 GHz and τf = 8.9 ppm/°C.