Abstract:The connection between the cleanliness of 52100 type bearing steels and their reliability has been well documented. Most research over the past 30 years has focused on sensitive compositional control during metallurgical refinement, leading to steels so clean that industrial cleanness standards are no longer suitable for quantifying further improvements. There is less literature, however, detailing the mechanism by which different impurities initiate rolling contact fatigue (RCF). Early work focused on comparing fatigue lives with cleanness ratings, which include a worst field analysis to determine the inclusion content and post-failure analysis to determine damage nucleation sites. The stress concentrations around discontinuities in the steel matrix can now however be visualised using computational modelling techniques. There is now a much clearer picture of how non-metallic inclusions (NMIs) nucleate fatigue damage by causing changes in the subsurface microstructure, including white etching regions in the form of butterflies. Size, morphology, distribution and type of inclusion are important factors for determining their role in RCF and the ability to control these variables could lead to improved performance. The inclusion character is greatly influenced by the steelmaking process, from initial melt through to casting, as well as hot deformation. While the impact of microchemical banding on RCF is not well understood, the effect of microsegregation on the phases that form can be modelled using simple calculations. Hot rolling techniques also influence the steel cleanliness, as NMIs can be plastically deformed or broken up and voids can be introduced around them, thus affecting the interface with the matrix. Understanding the microstructure evolution from materials characterisation and the ability to model the process could establish an optimum degree of rolling reduction. This could greatly aid the production of large bearings, as some manufacturers currently make them from very large ingots to achieve the necessary reduction ratio and therefore required level of performance.

A New Proposed Weibull Distribution of Inclusion Size and Its Correlation with Rolling Contact Fatigue Life of an Extra Clean Bearing Steel

Microstructural-based analysis of the unexpected differences in rolling contact fatigue behavior between SAE52100 and SAE4320

Investigation on Rolling Contact Fatigue of 55 Medium-Carbon Steel

Numerical analysis of rolling contact fatigue crack initiation Considering material microstructure

Effects of Cerium on Non-metallic Inclusions and Rolling Contact Fatigue Life of a High-Carbon Chromium Bearing Steel

A Comprehensive Model for Assessing the Impact of Steel Cleanliness on Bearing Performance

Effect of Primary Carbides on Rolling Contact Fatigue Behaviors of M50 Bearing Steel

Improving the reliability of highly loaded rolling bearings: the effect of upstream processing on inclusions

Bending Fatigue Behaviors Analysis and Fatigue Life Prediction of 20cr2ni4 Gear Steel with Different Stress Concentrations Near Non-metallic Inclusions

Influence of Non-Metallic Inclusions on Very High-Cycle Fatigue Performance of High-Strength Steels and Interpretation via Crystal Plasticity Finite Element Method

A 3D Finite Element Model of Rolling Contact Fatigue for Evolved Material Response and Residual Stress Estimation

Rolling contact fatigue behaviour of M50 bearing steel with rare earth addition

A new explanation of Rolling Contact Fatigue in bearing steels based on multiscale models

Rolling contact fatigue failure mechanism of bearing steel on different surface roughness levels under heavy load

The Relationship Between Inclusions Characteristic Parameters and Bending Fatigue Performance of 20cr2ni4a Gear Steel

Influence of original microstructure on rolling contact fatigue property of D2 wheel steel

Weibull Distribution to Evaluate the Reliability of PEEK Thrust Bearings under Rolling Contact Fatigue in Water

The Evolution of White Etching Cracks (WECs) in Rolling Contact Fatigue-Tested 100Cr6 Steel

Rolling Contact Fatigue Wear Behavior of Carbide-free Bainitic Steel

Influence Of Rough Surface On Damage Evolution And Fatigue Life Of M50-Bearing Steel Containing A Spherical Inclusion

Cyclic Constitutive Response and Effective S–N Diagram of M50 NiL Case-Hardened Bearing Steel Subjected to Rolling Contact Fatigue