Effects of Grain Size and Secondary Phase on Corrosion Behavior and Electrochemical Performance of Mg-3Al-5Pb-1Ga-Y Sacrificial Anode

Qiang Cui,Danqing Yi,Hongxuan Wang,Jiayi Zhang,Jiao Xu,Bin Wang
DOI: https://doi.org/10.1016/j.jre.2018.11.012
IF: 4.632
2019-01-01
Journal of Rare Earths
Abstract:Grains with size of 4.5-20.5 mm were studied for their corrosion behavior and electrochemical performance in a Mg-3Al-5Pb-1Ga-Y sacrificial anode using immersion testing, electrochemical measurements and microstructure analysis. The results show that fine-grained microstructure has higher chemical activity and more negative discharge potentials than coarse-grained samples. The sample with the smallest average grain size of 4.5 mu m exhibits corrosion current density of 7.473 x 10(-5) A/cm(2), and work potentials of -1.721 V at current density of 10 mA/cm(2). The density of grain boundaries and LAGBs increases with grain refinement, which leads to higher rates of dissolution and diffusion for the atoms. The secondary phases promote the occurrence of corrosion and improve the chemical activity of alloy due to their higher potential than the substrate. Higher corrosion rate and discharge activity are directly attributed to the higher density of grain boundaries and LAGBs, as well as the secondary phase. (C) 2019 Chinese Society of Rare Earths. Published by Elsevier B.V. All rights reserved.
What problem does this paper attempt to address?