Evolution of Β Mg17Al12 in Mg Al Zn Ag Alloy over Time

Ying Li,Chengwen Tan,Xiaodong Yu,Zhihua Nie,Xiuchen Zhao,Jianmin Han,Shenpo Yuan,Mingyu Zha,Chuanbin Guo,Fuchi Wang
DOI: https://doi.org/10.1016/j.msea.2019.03.094
2019-01-01
Abstract:In this study, the microstructure evolution of beta-Mg17Al12 in Mg-9Al-0.5Zn-0.12Ag alloys aged at 175 degrees C for 18, 36, and 72 h was investigated. The results indicate that beta-Mg17Al12 precipitates contain discontinuous precipitates and continuous precipitates. The interface between a discontinuous precipitation phase and the matrix appears with either a straight or a stepped morphology. Existing misorientation dislocations at a straight interface disappear with increasing aging time. For continuous precipitates, a [11 (5) over bar](beta)/ /[2 (1) over bar(1) over bar0](alpha), (41 (1) over bar)(beta)/ /(101 (1) over bar)(alpha) orientation relationship (OR) was observed, and a stereogram of this new OR was calculated, the results of which are discussed herein. As aging time is prolonged, the continuous precipitates grow, and their OR develops toward a common Burgers OR. The yield strengths of the alloys aged for 18 and 36 h exhibit no significant differences owing to a better strengthening effect achieved by the new OR in the 18-h aged samples than that of the Burgers and Potter OR. As the aging time approaches 72 h, a larger grain size reduces the yield strength of the alloy.
What problem does this paper attempt to address?