Abstract:High Temperature Superconducting (HTS) tapes have crucial applications for generating high magnetic fields with minimal power input. Given a single tape has a limited current-carrying capacity, stacked tapes are common, fabricated through methods like solder soldering or epoxy impregnation requiring heat treatment. In this work, we have investigated the efficient region for vacuum heat treatment applicable of commercial HTS tapes, analyzed the thermal degradation principles and accordingly proposed a controlled heat treatment process for stacked HTS tapes to achieve more precise regulation of the critical current (I_c). This heat treatment process was explored using a specialized multi-temperature zone vacuum system. Critical parameters in this process include heat treatment temperature, duration and pressure on the tape. A series of experiments were conducted at 77 K in a self-field to investigate how these parameters affect the superconductivity performance of stacked HTS tapes. Based on the experimental results, an optimal heat treatment process has been proposed. Under the current process, with the heat treatment temperature set at 200 °C, duration at 20 min, and pressure on the tape at 12 MPa, the samples exhibit favourable properties characterized by a smooth and neat appearance without defects such as pinholes or false soldering, and the superconductivity performance can be consistently maintained at more than 97%. The obtained measurements were compared with simulated results, demonstrating an error margin within 0.5%. Moreover, precise control of I_c is achieved, tailored to tape and stacking specifications, allowing manageable degradation as required. This heat treatment process for stacked HTS tapes holds significant importance, especially in the context of designing cable-in-conduit conductors (CICCs) fabricated with stacked HTS tapes. It serves as a valuable reference for further advancements in this field.

Characterization of I-c Degradation in Bent YBCO Tapes

V–I properties and n-value of degraded Bi-2223/Ag superconducting tapes

Bending–Peeling Method to Measure Interface Strength of YBCO Tape

Bending performance analysis on YBCO cable with high flexibility

Delamination Properties of YBCO Tapes Under Shear Stress Along the Width Direction

Fatigue Behavior of Critical Current Degradation for YBCO Tapes at 77 K

– properties and -value of degraded Bi-2223/Ag superconducting tapes

Continuous Critical Current Measurement of High-Temperature Superconductor Tapes with Magnetic Substrates Using Magnetic-Circuit Method.

The experimental research and analysis on the quench propagation of YBCO coated conductor and coil

In-Plane and Out-of-Plane Anisotropy in the Optical and Dielectric Properties of Yba2cu3o7-X Superconducting Film

In-field Superconducting Critical Current of Y0.5Gd0.5Ba2Cu3O7-σ Films Obtained by a Multi-Step Deposition Process

Two-Dimensional Anisotropic Model of YBCO Coated Conductors

Thermal degradation analysis and optimization of controlled heat treatment for stacked high temperature superconducting tapes

Current Distribution Mapping in Insulated (gd,y)bco Based Stabilizer-Free Coated Conductor after Ac Over-Current Test for R-Sfcl Application

Preparation of a YBCO Superconducting Tape by Pulsed Laser Deposition

Quench Propagation of YBCO Tapes of DC Superconducting Fault Current Limiter

Improvement of Surface Morphology and Superconducting Properties of YBCO Coated Conductor on Ni-W Tapes

Contactless Measurement of Critical Current of High Temperature Superconductor Tape by Magnetic Circuit.

Method and Apparatus for Continuous $i_{\rm C}$ Examination of HTS Tape Using Magnetic Circuit

Influence of Torsional Strain on the Bi-2212 Tapes and Round Wires under Background Field

Observation And Analysis Of Defects In Impregnated Ybco Racetrack Coil