Distinct phase-selective corrosions of Ti-48Al alloy in aqueous electrolyte and molten salt
Xiaohu Huang,P.S. Sankara Rama Krishnan,Kai Xiang Kuah,Tzee Luai Meng,Yee Ng,Hailong Liu,Siew Lang Teo,Rahul Karyappa,Ming Lin,Andrew Chun Yong Ngo,R.V. Ramanujan,Daniel J. Blackwood,Hongfei Liu
DOI: https://doi.org/10.1016/j.corsci.2024.111997
IF: 7.72
2024-03-21
Corrosion Science
Abstract:Corrosion of Ti-48Al alloys, consisting of γ-TiAl phase and α 2 -Ti 3 Al phase in lamellar structures, has been studied by electrochemical method at room temperature and molten salt method at elevated temperatures, respectively. Morphological, crystallographic, and microstructural studies provide direct evidence for γ-phase selective etching by the electrochemical corrosion at room temperature. In contrast, α 2 -phase selective etching of the Ti-48Al alloy occurred during molten salt corrosion, alongside α 2 -to-γ phase transformations at elevated temperatures. The distinct corrosion behaviors have been discussed and attributed to different chemical and physical properties between γ-TiAl and α 2 -Ti 3 Al phases within the Ti-48Al alloy.
materials science, multidisciplinary,metallurgy & metallurgical engineering