Effects of surface micro–galvanic corrosion and corrosive film on the corrosion resistance of AZ91–xNd alloys
Zheng Yin,Renhua He,Yang Chen,Zhou Yin,Kun Yan,Kun Wang,Hong Yan,Honggun Song,Chengxin Yin,Hongyu Guan,Chao Luo,Zhi Hu,Chassagne Luc
DOI: https://doi.org/10.1016/j.apsusc.2020.147761
IF: 6.7
2021-01-01
Applied Surface Science
Abstract:<p>The effects of surface micro–galvanic corrosion and corrosive film on the corrosion resistance of AZ91–xNd alloys was evaluated by scanning electron microscopy (SEM), scanning Kelvin probe force microscopy (SKPFM), and electrochemical measurements. The microstructural morphologies showed that the formations of Al<sub>2</sub>Nd and Al–Mn–Nd phases were observed in AZ91–Nd alloy. According to the results of SKPFM, the Nd–rich phases were slightly noble than the β–Mg<sub>17</sub>Al<sub>12</sub> phase but less than the Al–Mn phase. Consequently, AZ91–1.0Nd alloy with dispersed Nd–rich phases showed the largest polarization resistance values of 5129 Ω·cm<sup>2</sup>, about 3.9 times than that of AZ91 (1313 Ω·cm<sup>2</sup>). The main factors affecting the corrosion resistance of AZ91–xNd alloys were as follows: (i) the suppression of surface micro–galvanic couple corrosion, since the Volta potential difference (secondary phases/α–Mg) was reduced after Nd addition, the effect of surface micro–galvanic corrosion was weakened, thereby enhancing the corrosion resistance of the tested alloy (AZ91); (ii) corrosive film, the uniform corrosive film containing Nd<sub>2</sub>O<sub>3</sub> isolated the specimens and the electrolyte, which suppressed the penetration of harmful anions (OH<sup>–</sup>, <span class="math"><math>CO32-</math></span>) and inhibited the occurrence of surface micro–galvanic corrosion of AZ91–Nd alloys.</p>
chemistry, physical,physics, applied, condensed matter,materials science, coatings & films