Effect of Mn2+ on the anodic film and corrosion behavior of Pb-Ca-Sn alloy anode in copper electrowinning
Xiukai Wang,Yingzhuo Xu,Panpan Zhang,He Leng,Jin Dong,Buming Chen,Yapeng He,Sheng Chen,Hui Huang,Zhongcheng Guo,Ruidong Xu
DOI: https://doi.org/10.1016/j.hydromet.2021.105618
IF: 4.217
2021-06-01
Hydrometallurgy
Abstract:<p>In this paper, the effect of Mn<sup>2+</sup> (≤160 mg/L) on the anodic film properties and corrosion behavior of Pb-0.07%Ca-1.25%Sn anodes in acidic CuSO<sub>4</sub> electrolyte is clarified. The anode was polarized in an electrolyte containing different concentrations of Mn<sup>2+</sup> ions for 48 h to obtain a stable oxide film on the surface. The phase composition and morphology of the oxide layer formed on the Pb-0.07%Ca-1.25%Sn anode after polarization were characterized by the XRD, SEM, and EDS techniques. The influence of Mn<sup>2+</sup> (≤160 mg/L) on the electrochemical behavior of the Pb-0.07%Ca-1.25%Sn anode was investigated in 45 g/L Cu<sup>2+</sup> and 180 g/L H<sub>2</sub>SO<sub>4</sub> solution via cyclic voltammetry, galvanostatic polarization, Tafel, and EIS measurements. In addition, the anodic weight loss, film formation, and corrosion mechanism of the anode are also proposed. The results reveal that the film formed on the Pb-0.07%Ca-1.25%Sn anode exhibited a gradient Pb|PbSO<sub>4</sub>|α-PbO<sub>2</sub>|α-PbO<sub>2</sub>-β-MnO<sub>2</sub> layer in the Mn<sup>2+</sup>-containing electrolytes. Then, during the oxygen evolution reaction (OER), the gradient layer was oxidized to MnO<sub>2</sub>, which was irregularly attached to the surface of the substrate and increased the roughness of the film. The presence of Mn<sup>2+</sup> accelerated the corrosion of the anode in the electrolyte and reduced the anodic oxygen evolution potential. When the concentration of Mn<sup>2+</sup> ions reached 160 mg/L, the corrosion rate was increased by 62.3% despite the anode potential decreasing by 30 mV.</p>
metallurgy & metallurgical engineering