Effect of grain size uniformity and crystallographic orientation on the corrosion behavior of Mg-2Zn-1Al bar
Yujiao Wang,Yun Zhang,Haitao Jiang
DOI: https://doi.org/10.1016/j.matchar.2021.111374
IF: 4.537
2021-09-01
Materials Characterization
Abstract:In this paper, the effect produced by grain size uniformity and crystallographic orientation on the corrosion behavior of the extruded Mg-2Zn-1Al bar was probed by means of techniques such as OM, SEM, XRD, quasi-situ EBSD (Electron Back Scattered Diffraction), and an electrochemical test. The results obtained revealed a high possibility of corrosion nucleation at the grain boundaries; furthermore, preferential corrosion was exhibited by the coarse grains in comparison to the fine grains. The microstructure composed of bimodal grain size retained a higher corrosion rate than the one with uniform grain size, which is attributable to the increased electrochemical heterogeneity in alloys on a micro-scale and the non-uniformity corrosion product film. Prism-oriented grains tend to corrode preferentially in contrast to the basal-oriented grains. The longitudinal sections of the bar entailing a mixture of both the prismatic and the basal oriented grains, expressed a larger corrosion rate than the transverse sections that only consist of the prismatic planes, which could be attributed to the micro-galvanic corrosion activity triggered by the presence of multiple crystallographic orientations. The grain size uniformity factor tends to produce a more profound effect on the corrosion behavior of the bar than its crystallographic orientation.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing