Abstract:In this work, preparation of Cu-Ni/Nano-Al 2 O 3 composite coating with (111)-preferred orientation on the surface of the H64 brass via electrodeposition technique. Variation of the deposition current density was found to play a key role in the control of the microstructure and strongly influence the corrosion resistance of the composite coating. Electrochemical impedance spectroscopy results indicated that the increase of nano-alumina content in composite coating is caused by the change of polarization mode. Under different current densities, the Ni (111) plane is only preferred orientation and the relative texture coefficient reaches the highest value of 54.36% at 5 A•dm -2 . The crystallite size of these coatings is about 10–55 nm dependent on current density, and high current density could refine the size. The microstructure of the coating changed from cauliflower to spherical with increasing deposition current density. Moreover, the Cu-Ni/Nano-Al 2 O 3 composite coating obtained at 5 A•dm -2 increased the polarization resistance and coating resistance of the H64 brass by about 50% and 83%, respectively. The corrosion potential ( E corr ) of Cu-Ni/Nano-Al 2 O 3 composite coating is shifted towards the nobler direction from -1.191 V to -0.063 V (Ag/AgCl) with the current density increases. The corrosion mechanism of Cu-Ni/Nano-Al 2 O 3 composite coating has gone through two stages corresponding to two-time and three-time constant of EEC models, respectively. The Cu-Ni/Nano-Al 2 O 3 has large potential merits in field of corrosion.

Corrosion Behavior of Bulk Nanocrystalline Copper in Ammonia Solution

Electrochemical corrosion behavior of nanocrystalline copper bulk

Electrochemical Corrosion Behavior of Bulk Nanocrystalline Copper in Nitric Acid Solution

Electrochemical Corrosion Behavior and Surface Passivation of Bulk Nanocrystalline Copper in Alkaline Solution

Effect of Grain Size on Corrosion of Nanocrystalline Copper in NaOH Solution

Preparation and electrochemical corrosion behaviour of 3D large-sized nanocrystalline copper bulk in solutions with chloride ions

Effect of Sulfate Ions on Anodic Polarization Behavior of Nanocrystalline Copper Bulk

Kinetic Analysis on Anodic Polarization Behavior of Nanocrystalline Copper in Na2SO4 Solution

Corrosion Behavior of High-performance Crystalline CuCrZr/Amorphous CuZrAl Composites in NaCl Solution

Nanoscale Intergranular Corrosion and Relation With Grain Boundary Character as Studied In Situ on Copper

The corrosion study of 90Cu-10Ni (UNS C70600) materials in ammonia and sulfide environments

Influence of cryogenic impacting and succeeding annealing on electrochemical corrosion behavior of coarse-grain Cu bulk in sodium chloride solution

CORROSION BEHAVIOR OF Cu-Nb AND Ni-Nb AMORPHOUS FILMSPREPARED BY ION BEAM ASSISTED DEPOSITION

Effects of Cu-content and passivation treatment on the corrosion resistance of Al0.3CuxCoCrFeNi high-entropy alloys

Corrosion behaviors of amorphous and nanocrystalline Fe-based alloys in NaCl solution

Localized corrosion of thermally aged Cu-containing Ni-13Cr-10Fe alloys: The role of Cu enrichment induced grain boundary sensitization

Enhanced Corrosion Resistance of a Cu10Ni Alloy in a 3.5 Wt% NaCl Solution by Means of Ultrasonic Surface Rolling Treatment

Electrochemical Impedance Spectra for the Corrosion of Porous Cu-35mass%Ni-(5,10)mass%Cr Alloys in Molten (0.62li,0.38k)2co3 at 650 °C in Air

Relationship of Corrosion Behavior Between Single-Phase Equiatomic CoCrNi, CoCrNiFe, CoCrNiFeMn Alloys and Their Constituents in NaCl Solution

Corrosion Behavior of Two Heat Treatment Al-Zn-Mg-Cu Alloys in Different Intergranular Corrosion Solution

Electrochemical behavior and electro-crystallization mechanism of Cu-Ni/Nano-Al 2 O 3 coating with a deposition current density dependence