Abstract:The thermophysical properties of dense ZrB2-20 vol% SiC ceramics (ZS) with and without doping of 5 vol % WC (ZSW) were characterized up to 1800 degrees C. Because of the in-situ formed WB with low thermal conductivity and the strong phonon scattering effect from (Zr,W)B-2 solid solution, the thermal conductivity of ZSW (36.2 W/(m K)) at room temperature is much lower than that of ZS (100.4 W/(m K)), however, their differences at 1800 degrees C is very limited (42.2 W/(m K) for ZSW and 47.4 W/(m . K) for ZS). The detailed calculation indicates that contributions from lattice vibrations on the thermal conductivity decreased to nearly zero at 1800 degrees C in both samples, therefore, electrical conductivity of ZS and ZSW dominates their thermal transport behavior at higher temperatures. Furthermore, amorphous phase with compositions of Ca-Al-Si-O was occasionally found at the triple junction of ZS, its softening and rewetting of the grain boundary at higher temperature were confirmed from the internal friction curve and microstructural characterization at different levels, which was thought to be responsible for the tremendous increase of Interfacial thermal resistance and continuous drop of thermal conductivity of ZS up to 1800 degrees C. On the contrary, benefiting from the clean boundary and tight triple junction in ZSW, its thermal conductivity can stabilize between 36 and 47 W/(m K) in a broad temperature range from 25 to 1800 degrees C. Based on the measurement above, the type of carriers and thermoelectric figure of merit (zT) in ZrB2-SiC based ceramics are also firstly reported. (C) 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

High Thermal Conductivity of Pure Dense SiC Ceramics Prepared Via HTPVT

Preparation and Characterization of Pure SiC Ceramics by HTPVT Induced by Seeding with SiC Nanoarrays

Fabrication of highly dense pure SiC ceramics via the HTPVT method

Preparation and Characterization of Pure SiC Ceramics by High Temperature Physical Vapor Transport Induced by Seeding with Nano SiC Particles

Effects of Starting Materials on Preparation and Properties of Pure SiC Ceramics Via the HTPVT Method

High Thermal Conductivity in Pressureless Densified SiC Ceramics with Ultra-Low Contents of Additives Derived from Novel Boron–carbon Sources

Fabrication of Si3N4 Ceramics with High Thermal Conductivity and Flexural Strength Via Novel Two-Step Gas-Pressure Sintering

Thermal Conductivity and Microstructure Properties of Porous SiC Ceramic Derived from Silicon Carbide Powder

Properties and Microstructure of an HfB2-HfC-SiC Ultra High Temperature Ceramics

Fabrication of Si 3 N 4 ceramics with high thermal conductivity and flexural strength via novel two-step gas-pressure sintering

Porous 2h‐silicon Carbide Ceramics Fabricated by Carbothermal Reaction Between Silicon Nitride and Carbon

The Effect of Graphite Type on the Growth of Dense SiC Ceramics Prepared by the HTPVT Method

The Thermal, Electrical and Mechanical Properties of Porous Α-Sic Ceramics Bonded with Ti3SiC2 and Β-Sic Via Low Temperature In-Situ Reaction Sintering

Fabrication of Si3N4 ceramics with improved thermal conductivity by carbothermal reduction and two‐step sintering

Sintering of β-Si_3N_4 Powder and Thermal Conductivity of the Ceramic

Porous high-entropy (Zr0.25Hf0.25Nb0.25Ti0.25)C with high strength and uniform pore structure fabricated by freeze-casting

Thermal and Electrical Transport in ZrB2-SiC-WC Ceramics Up to 1800 °C

Low‐temperature reactive hot‐pressing of Ta0.2Hf0.8C‐SiC ceramics at 1700°C

Fabrication, Microstructure, and Properties of SiC/Al 4 SiC 4 Multiphase Ceramics Via an In-Situ Formed Liquid Phase Sintering

Preparation and properties of in situ TiC/corundum–mullite electrically conductive ceramic

Research progress in thermal conductivity of SiCceramics