Effect of He Ion Irradiation on the Microstructure of T′ Phase Yttria-Stabilized Zirconia Ceramic Coatings

Bo Liu,Jianxiong Zou,Liwei Lin,Shanlin Wang,Yu Bai,Chunhai Liu,Qiran Li
DOI: https://doi.org/10.1016/j.nimb.2018.04.042
2018-01-01
Abstract:Yttria-stabilized zirconia (YSZ) films with tetragonal (t') phase was prepared on China Low Activation Martensitic steel (CLAMs) substrates by supersonic atmospheric plasma spraying (SAPS) with ZrO2-8 wt% Y2O3 nano-powders as feedstock. This study deals with the subject of the structural modifications and phase transformations in t' phase YSZ coatings induced by implantation of low-energy (60 keV) He ions. It is found that the phase transformation in t' phase YSZ coatings during helium ion-irradiation as a function of fluence can be divided into a two-stage process based on the microstructural evolution as follows: (i) In the case of He ions at 0.5 x 10(17) cm(2) (similar to 1.5 dpa), no obvious volume swelling can be detected, suggesting the irradiation-induceddefects is primarily associated with a positive relaxation volume. Therefore, only t' -> t phase transformation was observed for the samples implanted at a fluence of 0.5 x 10(17) cm(-7) . (ii) While increasing the fluence from 0.5 x 10(17) cm(-2) to 2 x 10(17) cm(-2) , an increase in the defect concentrations can be observed, leading to an exponential growth in volume swelling from 3.2% to 9.7% observed. These high- density extended defects can induce a plastic deformation in the lattice structure, resulting significant lateral compressive stress. Correspondingly, the t' -> t + c phase transformation was detected for the samples implanted at the fluence of 2 x 10(17) cm(-2) . At a fluence of 10 x 10(17) cm(-2) , the formation of the He bubbles, and ellipsoidal cavities can be observed by TEM, inducing the further volume swelling. Meanwhile, the intensity of (400)(c) peak increases while fluence increase from 2 x 10(17) cm(-2) to 10 x 10(17) cm(-2) . Based on the experimental results, a reasonable mechanism for the phase transformation of t' phase YSZ samples during He ions irradiation is proposed.
What problem does this paper attempt to address?