Abstract:SiC layer was prepared in an industrial scale spout fluidized bed by chemical vapor deposition. The density of SiC coating was about 3.18 g/cm(3). High temperature oxidation experiments were carried out at different temperatures from 800 to 1600 degrees C. The microstructure and composition were characterized using different methods, including mass change weighing, XRD, EDS and SEM. It was found that the weight gain of SiC coating layer was not obvious below 1200 degrees C, and subsequent mass gain gradually increased with increasing temperature, reaching 10% at 1600 degrees C. High-magnification SEM results show that the oxidation began from the surface and gradually formed punctate distribution of the oxide. Small crystal structure (similar to micron) of the SiC surface was very clear at 1000 degrees C, and this crystal structure disappeared gradually at high temperatures, forming oxides of Si in the SiC surface. There was a stacking fault stress due to the different thermal expansion coefficients and elastic modulus of SiC and Si oxides, leading to the gradual formation of cracks around the punctates. With increasing temperature, the crack further increased the oxidation rate of SiC, and finally the formed Si oxides layer fell off from the particles. It can be seen clearly that the layer was peeling when the temperature was increased to 1400 degrees C. Increasing the temperature to 1600 degrees C, the SiC coating was oxidized completely into a honeycomb structure, with obvious sintering of SiC. XRD analysis shows that there was a growing SiO2 peaks from 1400 degrees C, indicating that surface oxidation was significant. EDS results shows that the oxygen content in the coating surface gradually increased with increasing temperature. Semi-quantitative analysis shows that the surface was close to SiO2 at 1600 degrees C.

In Situ Gas–Solid Reaction and Oxidation Resistance of Silicon Carbide Coating on Carbon Fibers

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

Oxidation resistance improvement of carbon fiber nonwoven fabrics through SiC coating technology

In-situ SiC nanowires reinforced SiC-based multicomponent ceramic coating for protecting SiOC/CF composites

High Temperature Oxidation Behavior of SiC Coating Materials

Long-time oxidation behavior of the nearly stoichiometric polycrystalline SiC fibers under air atmosphere at different temperatures

An oxidation protective coating prepared by SiC densifying HfB2-SiC skeleton for SiC-coated C/C composites at 1473, 1773, and 1973 K

Siliconization elimination for SiC coated C/C composites by a pyrolytic carbon coating and the consequent improvement of the mechanical property and oxidation resistances

Oxidation of SiC fibers in water vapor

Effect of the Incorporation of SiC Nanowire with Double Protective Layers on SiC Coating for C/C Composites

Deposition voltages on the phase evolutions, microstructures, and oxidation behaviors of thermal-resistance Glass-MoSi2-SiC coating

A gradient composite coating to protect SiC-coated C/C composites against oxidation at mid and high temperature for long-life service

A dense ZrB2-SiC-Si/SiC-Si coating to protect carbon/carbon composites against oxidation at 1773 K and 1973 K

Synthesis and characterization of high-temperature resistant yttrium-doped lanthanum monazite coatings on SiC fibers

Microstructure and corrosion behavior of in-situ grown Y3Si2C2 coated SiC fibers exposed to air and wet-oxygen at 1400 °C

Investigation on the oxidation and ablation behaviors of HfB2-SiC-Si/SiC-Si coatings for carbon/carbon composites

Comparison of Oxidation Behaviors of 3D C/PyC/SiC and SiC/PyC/SiC Composites in an O2-Ar Atmosphere

A Thick SiC-Si Coating Prepared by One-Step Pack Cementation for Long-Term Protection of Carbon/carbon Composites Against Oxidation at 1773 K

Improved antioxidative and mechanical properties of SiC coated C/C composites via a SiO2-SiC reticulated layer

Enhanced antioxidation and microwave absorbing properties of SiC/SiO2 coating on carbon fiber

Fabrication and oxidation resistance of mullite/yttrium silicate multilayer coatings on C/SiC composites