Synthesis and characterization of high-temperature resistant yttrium-doped lanthanum monazite coatings on SiC fibers

Peng Liu,Xi Tan,Hao Ren,Wei Liu,Linwen Jiang,Xiaofeng Zhang

DOI: https://doi.org/10.1016/j.surfcoat.2022.129183

IF: 4.865

2022-12-28

Surface and Coatings Technology

Abstract:To improve the long-term oxidation resistance of SiC fibers, a novel yttrium-doped lanthanum monazite (Y-LaPO 4 ) coating was deposited onto the surface of SiC fibers (Y-LaPO 4 /SiC f ) by a simple hydrothermal method. The static oxidation behavior of Y-LaPO 4 /SiC f , SiC fibers coated with lanthanum monazite (LaPO 4 /SiC f ), and SiC fibers without coatings (SiC f ) was studied at 1350 °C for 50 h. The results indicated that yttrium diffused into the oxide scale during oxidation process. The thicknesses of the oxide scales for the oxidized fibers in Y-LaPO 4 /SiC f and LaPO 4 /SiC f were about 4.56 and 11.31 μm. SiC fibers without coatings were completely oxidized to silica. Furthermore, the oxidation kinetic curves of SiC f , LaPO 4 /SiC f , and Y-LaPO 4 /SiC f exhibited a parabolic trend during oxidation for 15, 20, and 50 h. Calculated the oxidation rate constants of SiC f , LaPO 4 /SiC f , and Y-LaPO 4 /SiC f were found to be 1.37, 1.08, and 0.40 μm 2 /h, respectively. The system of Y-LaPO 4 coatings not only retains LaPO 4 as a framework of the interface, but also incorporates yttrium to improve the oxidation resistance of fibers. Therefore, doping yttrium in lanthanum monazite can enhance the adherence between coatings and oxide scales and improve the oxidation resistance of SiC fibers.

physics, applied,materials science, coatings & films