Abstract:Hot pressing was used to produce compact ceramic samples with the following composition (wt.%): 60 ZrB2 + 20 SiC + 20 (Al2O3 + 32 t-ZrO2). The tetragonal modification of zirconium oxide in the eutectic was stabilized by yttrium oxide. The porosity of the samples was 3–5%. The mechanical properties of the ceramics (hardness HV, fracture toughness KIc, tensile strength δf, compressive strength Y, grain-boundary strength S, and bending strength σ) were studied. Analysis of the microstructure and elemental composition of the phases revealed that a defect-free structure developed in the ZrB2-based composite through strong Van Der Waals adhesive interaction at the SiC–Al2O3 interface, which increased the fracture toughness to 9.4 MPa ∙ m1/2. In turn, this increased the grain strength from 0.64 GPa for the basic composite to 3.46 GPa for the ZrB2–SiC composite with an oxide addition. An addition of Al2O3 + 32 wt.% t-ZrO2 was introduced in sufficient quantities not only to reduce the fracture stress but also to promote plastic deformation of the material for high-temperature bending strength. Study of the oxidation process showed that the weight increment of the 60 wt.% ZrB2 + 20 wt.% SiC + 20 wt.% (Al2O3 + 32 wt.% t-ZrO2) sample at 1600°C for a holding time of 1 h was stabilized by dense oxide scale formed on the material, while the weight increment of the ZrB2 + 20 wt.% SiC sample and, consequently, the scale thickness increased monotonically. The scale that formed on the ZrB2 + 20 wt.% SiC samples with an addition of Al2O3 + 32 wt.% t-ZrO2 consisted of an upper Al2SiO5-based layer 50 μm thick with ZrO2 inclusions and a lower ZrO2-based layer up to 80 μm thick with Al2SiO5 inclusions. The eutectic Al2O3 + 32 wt.% t-ZrO2 oxide addition to the basic ZrB2–SiC system had higher oxidation resistance and thus prevented the diffusion of oxygen into the material.

Oxidation Behaviour of ZrB2–SiC (al/y) Ceramics at 1700 °C

Oxidation Kinetics of Hot-Pressed ZrB2–SiC Ceramic Matrix Composites

Oxidation Behavior of ZrB2–SiC–ZrO2 Ceramic Composites in the Temperature Range of 800–1200°C

Oxidation Behavior of Hot Pressed ZrB2‐ZrC‐SiC Ceramic Composites

Oxidation behavior of zirconium diboride–silicon carbide at 1800°C

High‐Temperature Oxidation at 1900°C of ZrB2–xSiC Ultrahigh‐Temperature Ceramic Composites

Oxidation Behavior of ZrC-based Composites in Static Laboratory Air Up to 1300 °C

Isothermal Oxidation of Zr2[Al(Si)]4C5–SiC Composites at 1000–1300°C in Air

High-Temperature Oxidation Resistance of ZrB2-SiC Ceramic Composites Prepared by Reactive Hot Pressing

Oxidation Properties of ZrB2-20vol.%SiC-10vol.%BN Ceramic Composite at 1200°C

Oxidation Behaviors of the Pressureless Sintered ZrB<SUB>2</SUB>-SiC Composites: Oxidation Behaviors of the Pressureless Sintered ZrB<SUB>2</SUB>-SiC Composites

Design and Preparation of an Ultra-High Temperature Ceramic by In-Situ Introduction of Zr2[Al(Si)]4C5 into ZrB2-SiC: Investigation on the Mechanical Properties and Oxidation Behavior

Oxidation Resistance of Zr2(Al(Si))4C5-based Composites at Ultra-High Temperature

Oxidation Resistance Behavior of Short Carbon Fiber Reinforced ZrB2,-SiC Composites

Oxidation-resistant ZrB2–SiC composites at 2200°C

Preparation and flame ablation/oxidation behavior of ZrB2/SiC ultra-high temperature ceramic composites

Oxidation Resistance Performance of ZrB_2-SiC Ceramic Matrix Composites

High-temperature Oxidation Behavior of Monolithic Zr3[Al(Si)]4C6 and Its Composite Incorporating 30vol% ZrB2-SiC: Providing a Basis for Broadening the Service Temperature

Mechanical and Corrosion Properties of ZrB2–SiC Composite Ceramics with Oxide Additions

Effect of Zr2Al4C5 Content on the Mechanical Properties and Oxidation Behavior of ZrB2-SiC-Zr2Al4C5 Ceramics

Oxidation Behaviour of C–SiC–ZrC Composite