Abstract:Atom probe microscopy was used to generate tomographic analyses of solute clustering and precipitation reactions in a Ti–Mo added microalloyed steel under simulated strip-rolling conditions. It was observed that the interphase row spacing of precipitates was reduced with the application of a pre-strain. The atom probe data also revealed the coexistence of nanoclusters and precipitate particles, even after isothermal holding for 3600s. These microstructural features occurred both within 3-D interphase precipitate sheets, and in randomly selected fields of view. A bimodal distribution of larger (∼8–10nm) precipitates coexisted with smaller nanoclusters (∼3nm) within the interphase sheets/rows. Both the nanoclusters and the precipitates possessed a disc morphology, although nanoclusters with less than ∼30 atoms were more irregular in shape. The size of the nanoclusters and the precipitates was expressed as a Guinier radius, and this varied between 0.5 and 8nm for both strain conditions, with the average size ∼1.8nm. The composition of the nanoclusters varied over a wide range, yet was mostly rich in C. All of the nanoclusters and precipitates consisted of a mixture of Ti, Mo and C and the average precipitate composition was close to that of MC carbide stoichiometry, where M represents a mixture of Ti and Mo. In the majority of cases, the Ti/Mo ratio in the MC carbides was>1. As the Guinier radius increased above 2.5nm, the composition range became narrower, towards the MC carbide stoichiometry, with a small amount of Fe (∼3–12at.%).

Decelerated Coarsening of (ti, Mo)C Particles with a Core–Shell Structure in Austenite of a Ti-Mo-Bearing Steel

Evolution of (ti, Mo)C Particles in Austenite of a Ti–Mo-bearing Steel

Carbide Precipitation in Austenite of a Ti–Mo-containing Low-Carbon Steel During Stress Relaxation

Precipitation Behavior and Strengthening Effect of (Ti,Mo)C Particles in a Martensitic Steel

Revealing the influence of Mo addition on interphase precipitation in Ti-bearing low carbon steels

Effect of Molybdenum Addition on the Precipitation of Carbides in the Austenite Matrix of Titanium Micro-Alloyed Steels

Refinement mechanism of nanoscale Cu-rich precipitates by Mo addition and its effect on strength-toughness of Cu-bearing low carbon high strength steel

Phenomenal Effect of Stable (Ti, Mo)C Nano-Sized Precipitates in Retarding the Recrystallization and Grain Growth in High-Strength Ferritic Steel

Microstructure evolution, mechanical properties, and corrosion behavior of in-situ TiC/TC4 composites through Mo addition

Effect of Mo on Microstructures and Wear Properties of In Situ Synthesized Ti(C,N)/Ni-Based Composite Coatings by Laser Cladding

Three-dimensional atom probe microscopy study of interphase precipitation and nanoclusters in thermomechanically treated titanium–molybdenum steels

Effect of V on the Precipitation Behavior of Ti−Mo Microalloyed High-Strength Steel

Carbide Precipitation in Austenite of a Titanium-Tungsten-Bearing Low-Carbon Steel

Effect of cobalt on precipitation in Fe-Cr-Co-Mo-Ni-C stainless steels

The effect of Ti–Mo–Nb on the microstructures and tensile properties of a Fe–Mn–Al–C austenitic steel

Coarsening behavior of the Ti2Cu phase of a Ti-14Cu alloy during isothermal thermal exposure

Hardening Through an Ultrafine Carbide Precipitation in Austenite of a Low-Carbon Steel Containing Titanium and Tungsten

Effect of TaC Particles Dissolution on Grain Coarsening in Reduced Activation Steels

Strengthening the grain boundary of Mo alloy via little TiC addition

Austenite Layer and Precipitation in High Co–Ni Maraging Steel

Effect of Mo addition on microstructure and wear resistance of laser clad AlCoCrFeNi-TiC composite coatings