Morphological evolution of Ti2Cu in Ti-13Cu-Al alloy after cooling from semi-solid state
Dong Zhao,Yongnan Chen,Chaoping Jiang,Yao Li,Qinyang Zhao,Yiku Xu,Haifei Zhan,Mingpan Wan,Yongqing Zhao
DOI: https://doi.org/10.1016/j.jallcom.2020.156639
IF: 6.2
2020-12-01
Journal of Alloys and Compounds
Abstract:<p>The mechanical performance of Ti-13Cu-Al alloy is highly determined by its microstructure, which is significantly affected by the cooling process from semi-solid state as it induces peritectic solidification and the subsequent eutectoid transformation of the alloy. This work investigated the effects of cooling rates on the morphology of Ti<sub>2</sub>Cu phase and mechanical properties of Ti-13Cu-Al alloy after cooling from semi-solid state (β+L phase). Different cooling mediums have been considered, including furnace cooling (0.5 °C/s), air cooling (50 °C/s) and water cooling (150 °C/s), corresponding to a slow, normal and rapid cooling process, respectively. It is found that α+Ti<sub>2</sub>Cu phases are uniformly distributed in the alloy after different cooling processes, and the morphology of Ti<sub>2</sub>Cu phase is controlled by the peritectic solidification and eutectoid transformation. Specifically, the thickness and the volume fraction of primary Ti<sub>2</sub>Cu phase are larger than the sample cooling from β phase field when the cooling rate is the same. The morphology of Ti<sub>2</sub>Cu phase varies from "laths + blocky + sheaves" to "short laths + blocky + rodlike" as the cooling rate gradually increases. It is further revealed that the β/L interface provides a fast channel for solute atom diffusion, and the peritectic Ti<sub>2</sub>Cu phase provides a favorable nucleation site for the precipitation of eutectoid Ti<sub>2</sub>Cu. Based on the tensile property and hardness examinations, the mechanical properties of the Ti-13Cu-Al alloy show a clear dependency with the precipitation of Ti<sub>2</sub>Cu phase after cooling from semi-solid state, indicating the importance of cooling mode from semi-solid state on the microstructure and mechanical properties of the alloy.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering