Abstract:Atom probe microscopy was used to generate tomographic analyses of solute clustering and precipitation reactions in a Ti–Mo added microalloyed steel under simulated strip-rolling conditions. It was observed that the interphase row spacing of precipitates was reduced with the application of a pre-strain. The atom probe data also revealed the coexistence of nanoclusters and precipitate particles, even after isothermal holding for 3600s. These microstructural features occurred both within 3-D interphase precipitate sheets, and in randomly selected fields of view. A bimodal distribution of larger (∼8–10nm) precipitates coexisted with smaller nanoclusters (∼3nm) within the interphase sheets/rows. Both the nanoclusters and the precipitates possessed a disc morphology, although nanoclusters with less than ∼30 atoms were more irregular in shape. The size of the nanoclusters and the precipitates was expressed as a Guinier radius, and this varied between 0.5 and 8nm for both strain conditions, with the average size ∼1.8nm. The composition of the nanoclusters varied over a wide range, yet was mostly rich in C. All of the nanoclusters and precipitates consisted of a mixture of Ti, Mo and C and the average precipitate composition was close to that of MC carbide stoichiometry, where M represents a mixture of Ti and Mo. In the majority of cases, the Ti/Mo ratio in the MC carbides was>1. As the Guinier radius increased above 2.5nm, the composition range became narrower, towards the MC carbide stoichiometry, with a small amount of Fe (∼3–12at.%).

Effect of Molybdenum Addition on the Precipitation of Carbides in the Austenite Matrix of Titanium Micro-Alloyed Steels

Revealing the influence of Mo addition on interphase precipitation in Ti-bearing low carbon steels

Effect of V on the Precipitation Behavior of Ti−Mo Microalloyed High-Strength Steel

Carbide Precipitation in Austenite of a Ti–Mo-containing Low-Carbon Steel During Stress Relaxation

Precipitation Behavior and Strengthening Effect of (Ti,Mo)C Particles in a Martensitic Steel

The effect of Ti–Mo–Nb on the microstructures and tensile properties of a Fe–Mn–Al–C austenitic steel

Effect of Mo on Nano‐Precipitation Behavior and Microscopic Mechanical Characteristics of Ferrite

Carbide Precipitation in Austenite of a Titanium-Tungsten-Bearing Low-Carbon Steel

Effect of Mn concentration on the kinetics of strain induced precipitation in Ti microalloyed steels

Evolution of (ti, Mo)C Particles in Austenite of a Ti–Mo-bearing Steel

Effect of cobalt on precipitation in Fe-Cr-Co-Mo-Ni-C stainless steels

Effect of 2–6 At.% Mo Addition on Microstructural Evolution of Ti-44Al Alloy

Three-dimensional atom probe microscopy study of interphase precipitation and nanoclusters in thermomechanically treated titanium–molybdenum steels

Microstructure evolution, mechanical properties, and corrosion behavior of in-situ TiC/TC4 composites through Mo addition

Microstructural evolution and grain refinement in an intermetallic titanium aluminide alloy with a high molybdenum content

Influence of Mo doping on the tribological behavior of Ti3AlC2 ceramic at different temperatures

Effect of TiC content on the microstructure and mechanical properties of Ti-30Mo-xTiC composites

Strengthening the grain boundary of Mo alloy via little TiC addition

Decelerated Coarsening of (ti, Mo)C Particles with a Core–Shell Structure in Austenite of a Ti-Mo-Bearing Steel

Influence of TiC contents on the microstructure, mechanical properties, and oxidation behavior of Mo–10Si–8B alloys

Phenomenal Effect of Stable (Ti, Mo)C Nano-Sized Precipitates in Retarding the Recrystallization and Grain Growth in High-Strength Ferritic Steel