Abstract:Atom probe microscopy was used to generate tomographic analyses of solute clustering and precipitation reactions in a Ti–Mo added microalloyed steel under simulated strip-rolling conditions. It was observed that the interphase row spacing of precipitates was reduced with the application of a pre-strain. The atom probe data also revealed the coexistence of nanoclusters and precipitate particles, even after isothermal holding for 3600s. These microstructural features occurred both within 3-D interphase precipitate sheets, and in randomly selected fields of view. A bimodal distribution of larger (∼8–10nm) precipitates coexisted with smaller nanoclusters (∼3nm) within the interphase sheets/rows. Both the nanoclusters and the precipitates possessed a disc morphology, although nanoclusters with less than ∼30 atoms were more irregular in shape. The size of the nanoclusters and the precipitates was expressed as a Guinier radius, and this varied between 0.5 and 8nm for both strain conditions, with the average size ∼1.8nm. The composition of the nanoclusters varied over a wide range, yet was mostly rich in C. All of the nanoclusters and precipitates consisted of a mixture of Ti, Mo and C and the average precipitate composition was close to that of MC carbide stoichiometry, where M represents a mixture of Ti and Mo. In the majority of cases, the Ti/Mo ratio in the MC carbides was>1. As the Guinier radius increased above 2.5nm, the composition range became narrower, towards the MC carbide stoichiometry, with a small amount of Fe (∼3–12at.%).

Carbide Precipitation in Austenite of a Ti–Mo-containing Low-Carbon Steel During Stress Relaxation

Evolution of (ti, Mo)C Particles in Austenite of a Ti–Mo-bearing Steel

Carbide Precipitation in Austenite of a Titanium-Tungsten-Bearing Low-Carbon Steel

Effect of Molybdenum Addition on the Precipitation of Carbides in the Austenite Matrix of Titanium Micro-Alloyed Steels

Precipitation Behavior and Strengthening Effect of (Ti,Mo)C Particles in a Martensitic Steel

Revealing the influence of Mo addition on interphase precipitation in Ti-bearing low carbon steels

Decelerated Coarsening of (ti, Mo)C Particles with a Core–Shell Structure in Austenite of a Ti-Mo-Bearing Steel

Strain-induced Precipitation in a Ti Micro-Alloyed HSLA Steel

Interphase precipitation behavior of nano-sized carbides in low carbon steel

Effect of Mn concentration on the kinetics of strain induced precipitation in Ti microalloyed steels

Effect of V on the Precipitation Behavior of Ti−Mo Microalloyed High-Strength Steel

Phenomenal Effect of Stable (Ti, Mo)C Nano-Sized Precipitates in Retarding the Recrystallization and Grain Growth in High-Strength Ferritic Steel

Hardening Through an Ultrafine Carbide Precipitation in Austenite of a Low-Carbon Steel Containing Titanium and Tungsten

Co-Precipitation Behavior in Ferrite Region During Isothermal Process in Ti-Mo-Cu Microalloyed Steel

Effect of Mo content on the thermal stability of Ti-Mo-bearing ferritic steel

The effect of Ti–Mo–Nb on the microstructures and tensile properties of a Fe–Mn–Al–C austenitic steel

Carbide Precipitation during Processing of Two Low-Alloyed Martensitic Tool Steels with 0.11 and 0.17 V/Mo Ratios Studied by Neutron Scattering, Electron Microscopy and Atom Probe

Effect of Mo on Nano‐Precipitation Behavior and Microscopic Mechanical Characteristics of Ferrite

Three-dimensional atom probe microscopy study of interphase precipitation and nanoclusters in thermomechanically treated titanium–molybdenum steels

Correlation between Precipitation and Recrystallisation during Stress Relaxation in Titanium Microalloyed Steel

Microstructure evolution, mechanical properties, and corrosion behavior of in-situ TiC/TC4 composites through Mo addition