Abstract:In this study, G-phase strengthened 7Ni maraging alloys were studied using a combination of thermodynamic prediction based on the TCFE-7 database and advanced experimental techniques, including micro-hardness testing, electron backscatter diffraction (EBSD), in-situ X-ray diffraction (XRD), transmission electron microscopy (TEM), and atom probe tomography (APT). The martensite reversion and phase stability of overcooled austenite were precisely determined for a series of Fe-7Ni-2Si-based alloys, validating the effectiveness of thermodynamic predictions in martensite transformation. Based on these theoretical prediction, aging hardness measurements and microstructural observations further revealed that Ni 16 X 6 Si 7 -G (X=Ti, Nb, Ta) precipitates are effective strengthening phases in 7Ni maraging steel, with the exception of Ni 16 X 6 Si 7 (X=Mn, Zr) due to their significantly different thermal stabilities. Experimental results showed that the Ni 16 X 6 Si 7 -G (X=Ti, Nb, Ta) precipitates remained stable and densely distributed within the martensitic matrix after aging at 500 °C, resulting in high aging hardness values ranging from 350 to 550 HV. Among the studied alloys, the 1Ti alloy strengthened by the Ni 16 Ti 6 Si 7 -G phase exhibited the finest particle radius (estimated at 1.4 nm) and the highest number density (estimated at 1.9 × 10 24 /m 3 ). Additionally, it is worth noting that the Ni 16 Zr 6 Si 7 -G phase was believed to form through eutectic reaction with α-Fe during solidification and the Ni 16 Mn 6 Si 7 -G phase was only stable at temperatures below 460 °C and was not detected experimentally. These findings enhance our comprehension of G-phase precipitation and strengthening in 7Ni maraging steel and underscore the potential for utilizing thermodynamic calculations and advanced experimental techniques to guide the design and optimization of high-strength alloys.

Austenite Layer and Precipitation in High Co–Ni Maraging Steel

The Role of Al/Ti in Precipitate-Strengthened and Austenite-Toughened Co-Free Maraging Stainless Steel

Effect of Co content on microstructure and mechanical properties of maraging steel

Effects of Ni on Austenite Stability and Fracture Toughness in High Co-Ni Secondary Hardening Steel

Effect of cobalt on precipitation in Fe-Cr-Co-Mo-Ni-C stainless steels

Co-precipitated Ni/Mn Shell Coated Nano Cu-rich Core Structure: A Phase-Field Study

Influence of Grain Boundary Carbides on Mechanical Properties of High Nitrogen Austenitic Stainless Steel

Nano-sized Austenite and Cu Precipitates Formed by Using Intercritical Tempering Plus Tempering and Their Effect on the Mechanical Property in a Low Carbon Cu Bearing 7 Ni Steel

Strengthening of Ni-Mn-Cu-Al-Co steel by nanoscale Cu and β-NiAl co-precipitated couples

Carbide Precipitation in Austenite of a Titanium-Tungsten-Bearing Low-Carbon Steel

Precipitation and reverted austenite formation in maraging 350 steel: competition or cooperation?

Carbide Precipitation and Element Distribution in High Co–Ni Secondary Hardening Steel

Effect of Aging on Transformation Behavior of Reverted Austenite and Toughness in Co-Free Maraging Stainless Steel

Precipitation behavior of the G-phase strengthened 7Ni maraging steels

Characterization and Numerical Simulation of Nucleation–growth–coarsening Kinetics of Precipitates in G115 Martensitic Heat Resistance Steel During Long-Term Aging

Reinforced Cu Precipitation Strengthening by Matrix Transformation from Martensite to Austenite in High-Strength Low-Alloy Steel

Influences of Cu on Microstructure and Mechanical Properties in Fe–Ni–Al Ultra-Strong Maraging Steels

Compositional and structural characterization of alloyed carbide by 3D atom probe and high-resolution TEM

Unveiling the Precipitate Evolutions and Relationships Between the Nano-Precipitates and Mechanical Properties in PH13–8Mo Stainless Steel

M5C2 Carbide Precipitates in a High-Cr Martensitic Steel

Deformation mechanism of a strong and ductile maraging steel investigated using in-situ X-ray synchrotron diffraction